Nanocrystalline thin cobalt films with perpendicular anisotropy were investigated.
The morphological and magnetic domain structures were studied in detail.
The average grain size and domain width increase with increasing film thickness.
70 nm thick films and thicker have fully perpendicular magnetization.
60 nm thick films possess clearly dominating perpendicular magnetization component.