文摘
The flexural strength (FS) of C2G3C2 is 83% higher than G7, when tested at RT. Lowering in FS with higher T is more for FRP with higher carbon content. The onset of glass transition was delayed with increase in hybrid ratio. C7 exhibits a lower ɛinst and higher ɛtime over G7 at higher T. At 110 °C, Creep resistance is superior in C2G5/G5C2 than both G7 and C7.