Large SiC solubilities in quasi-binary Cr–SiC system were measured. SiC solubilities was reproduced using a sub-regular solution model. Rapid growth of SiC of 720 µm/h at 1803 K was obtained by unary Cr solvent. SiC growth rates were proportional to solubility difference of carbon.