Investigation on F_R(LT)–F_R(HT) phase transition and pyroelectric properties of pulsed laser deposited Pb(Zr_0.93Ti_0.07)O₃ thin films

详细信息    查看全文

• 作者：Hui Zeng ; ^a ; ^{bestlich@163.com"" rel=""nofollow} ; ^{254419118@qq.com"" rel=""nofollow} ; Ping Wu^a ; Peng Zhang^a ; Daxing Dong^a
• 关键词：Zr-rich PZT thin films ; PZT/YBCO heterojunctions ; Pyroelectric ; PLD ; Infrared detection
• 刊名：Infrared Physics and Technology
• 出版年：2011
• 出版时间：September 2011
• 年：2011
• 卷：54
• 期：5
• 页码：422-426
• 全文大小：513 K

文摘

The preparation process, crystallinity and electrical properties of pulse laser deposited Pb(Zr_xTi_1−x)O₃ (PZT) thin films were investigated in this paper. PZT (x = 0.93) thin film samples deposited at different substrate temperatures were prepared. Si (1 1 0) was the substrate; Ag and YBCO were the top electrode and the bottom electrode respectively. The bottom electrode YBCO was deposited on the Si substrate by pulsed laser deposition (PLD), and then PZT was epitaxially deposited on YBCO also by PLD. After annealing, the top electrode Ag was prepared on PZT by thermal evaporation, and then the Ag/PZT/YBCO/Si structured thin films were obtained. The XRD and the analysis of their electrical characters showed that, when the substrate temperature was elevated from 600 °C to 800 °C, the crystallinity and electrical properties of PZT thin films became better and better, and the F_R(LT)–F_R(HT) phase transition of PZT (x = 0.93) thin films occurred at 62 °C. The PZT film deposited at 800 °C had the best pyroelectric properties, and when the F_R(LT)–F_R(HT) phase transition of this film occurred, the peak value of pyroelectric coefficient (p) was obtained, with a value of 1.96 × 10⁻⁶ C/(cm² K). The PZT film deposited at 800 °C had the highest remnant polarization (P_r) and the lowest coercive field (E_c), with the values of 34.3 μC/cm² and 41.7 kV/cm respectively.