12 % efficiency was obtained for 11 µm thick, liquid-phase crystalized Si on glass.
Using KOH texturing and anti-reflection foil, a JSC of 28.9 mA/cm2 was achieved.
Current density losses were characterized using LBIC, optics, EQE and simulations.
Main loss factors were direct reflection, the absorber contact and recombination.
Max. light trapping potential was almost reached, using a backside pyramid texture.