In this work, a higher concentration of Ti ions are incorporated into hydrothermally grown Ti-doped (2.2% by atomic ratio) micro-nanostructured hematite films by an in situ solid-state reaction method. The doping concentration is improved from 2.2% to 19.7% after the in situ solid-state reaction. X-ray absorption analysis indicates the substitution of Fe ions by Ti ions, without the generation of Fe2+ defects. Photoelectrochemical impedance spectroscopy reveals the dramatic improvement of the electrical conductivity of the hematite film after the in situ solid-state reaction. As a consequence, the photocurrent density increases 8-fold (from 0.15 mA/cm2 to 1.2 mA/cm2), and it further increases up to 1.5 mA/cm2 with the adsorption of Co ions. Our findings demonstrate that the in situ solid-state reaction is an effective method to increase the doping level of Ti ions in hematite films with the retention of the micro-nanostructure of the films and enhance the photocurrent.
Keywords:
in situ solid-state reaction method; Ti-doped hematite; photocurrent enhancement; Co ions adsorption