作者单位:Heng Wang (1) Peng Xiang (1) Mi Xu (1) Guanghui Liu (1) Xiong Li (1) Zhiliang Ku (1) Yaoguang Rong (1) Linfeng Liu (1) Min Hu (1) Ying Yang (1) Hongwei Han (1)
1. Michael Gr?tzel Center for Mesoscopic Solar Cells, Wuhan National Laboratory for Optoelectronics, Huazhong University of Science and Technology, Wuhan, 430074, China
ISSN:2095-2767
文摘
A monobasal solid-state dye-sensitized solar cell (ssDSC) with mesoporous TiO2 beads was developed and an efficiency of 4% was achieved under air mass (AM) 1.5 illumination. Scattering properties and electron diffusion coefficients of TiO2 mesoporous beads and P25 nanoparticles were investigated. The results show that TiO2 mesoporous beads display higher scatterance than P25 nano-particles, and TiO2 mesoporous beads have higher electron diffusion coefficients (2.86 ?10?5 cm2??1) than P25 nano-particles (2.26 ?10?5 cm2??1).