摘要
为提高氧化木薯淀粉(OTS)的使用性能,在碱性条件下,以3-氯-2-羟丙基磺酸钠和3-氯-2-羟丙基三甲基氯化铵为醚化剂,与OTS反应制备了氧化-双重醚化改性木薯淀粉(ODES),使用傅里叶变换红外光谱(FTIR)对其进行了表征分析,并研究了共混比对其与聚乙烯醇(PVA)复合材料的薄膜、黏合等性能的影响规律。结果表明,PVA与ODES共混对复合膜的性能具有显著的影响,膜的断裂伸长率分别由PVA与ODES共混质量比0∶100的3. 37%提升到80∶20的134. 4%,断裂强度逐渐降低,表明复合膜具有良好的柔韧性;共混后对棉和聚乳酸粗纱的黏合性能得到了显著提升。
To improve the performance of oxidized tapioca starch( OTS), oxidized and doubly etherified starch( ODES) was prepared by the reaction of OTS with sodium 3-chloro-2-hydroxypropyl sulfonate and 3-chloro-2-hydroxypropyl trimethyl ammonium chloride under alkaline condition. The ODES granules were analyzed by Fourier transform infrared( FTIR) spectroscopy. The influence of blending ratio on the properties of composite film and adhesion of the ODES/polyvinyl alcohol( PVA) was investigated.The results show that the blending of PVA and ODES has a significant effect on the properties of the composite films. When the blending ratio of PVA and ODES changes from 0 ∶ 100 to 80 ∶ 20,the breaking elongation of the films increases from 3. 37% to 134. 4%. The breaking strength of the films decreases gradually,which indicates that the ODES/PVA composite films have good flexibility. The adhesion exhibits an obvious improvement after the blending.
引文
[1]MARAN J P,SIVAKUMAR V,SRIDHAR R,et al.Development of model for mechanical properties of tapioca starch based edible films[J].Ind Crops Prod,2013,42(1):159-168.
[2]周永元.纺织浆料学[M].北京:中国纺织工业出版社,2004:1-12.
[3]ZHU Z F,CHENG Z Q.Effect of inorganic phosphates on the adhesion of mono-phosphorylated cornstarch to fibers[J].Starch-Strke,2008,60(6):315-320.
[4]夏鹏,徐亚雷,侯连龙.全生物降解淀粉塑料的研究进展[J].中国塑料,2012,26(12):8-13.
[5]乔志勇,祝志峰.磷酸酯淀粉/聚丙烯酸酯共混膜的织态结构与性能[J].高分子材料科学与工程,2009,25(8):72-75.
[6]李伟,祝志峰.电位和变性程度对季铵阳离子醚化-磺基丁二酸酯化淀粉薄膜性能的影响[J].高分子材料科学与工程,2015,31(11):70-74.
[7]祝志峰.纺织工程化学[M].上海:东华大学出版社,2010:179-217.
[8]杨明杰,沈艳琴,武海良,等.山梨醇对氧化淀粉浆料性能的影响[J].棉纺织技术,2016,44(2):32-35.
[9]ZHU Z F,ZHENG H,LI X C.Effects of succinic acid cross-linking and mono-phosphorylation of oxidized cassava starch on its paste viscosity stability and sizability[J].Starch-Strke,2013,65(9-10):854-863.
[10]LI W,XU W Z,WEI A F,et al.Quaternization/maleation of cornstarch to improve its adhesion and film properties for warp sizing[J].Fibers Polym,2016,17(10):1589-1597.
[11]ZHU Z F,CHEN P H.Carbamoyl ethylation of starch for enhancing the adhesion capacity to fibers[J].J Appl Polym Sci,2007,106(4):2763-2768.
[12]ZHU Z F,SHEN S Q.Effect of amphoteric grafting branch on the adhesion of starch to textile fibers[J].J Adhes Sci Technol,2014,28(17):1695-1710.
[13]CHANG Y J,CHOI H W,KIM H S,et al.Physicochemical properties of granular and non-granular cationic starches prepared under ultra high pressure[J].Carbohydr Polym,2014,99(1):385-393.
[14]谢晶曦.红外光谱在有机化学和药物化学中的应用[M].北京:科学出版社,1987:337-346.
[15]HAN X Z,CHEN S S,HU X G.Controlled-release fertilizer encapsulated by starch/polyvinyl alcohol coating[J].Desalination,2009,240(1):21-26.
[16]XU F L,LI Y B,WANG X J,et al.Preparation and characterization of nano-hydroxyapatite/poly(vinyl alcohol)hydrogel biocomposite[J].J Mater Sci,2004,39(18):5669-5672.