摘要
针对304不锈钢表面的快速电化学蚀刻图文标记方法进行了研究。探讨了电解液浓度、抗蚀膜层建立、蚀刻温度及时间对不锈钢蚀刻质量及效果的影响。确定了电化学蚀刻不锈钢的工艺条件下,实验在工件表面上快速蚀刻出清晰的图案,蚀刻槽呈平整均匀的银白色。蚀刻过程中电解液及产生的废液均很少,符合清洁生产及环境保护的要求。
A fast electrochemical etching method on the surface of 304 stainless steel were studied in this paper.The effects of electrolyte concentration,corrosion resistant film layer,etching temperature and time on the quality and effect of stainless steel etching were discussed.The process conditions of electrochemical etching stainless steel were determined.A clear pattern is quickly etched on the surface of stainless steel,and the etching groove is flat and even silver-white.In the process of etching,the electrolyte and the waste liquid produced are very few,which conforms to the requirements of cleaner production and environmental protection.
A fast electrochemical etching method on the surface of 304 stainless steel were studied in this paper.The effects of electrolyte concentration,corrosion resistant film layer,etching temperature and time on the quality and effect of stainless steel etching were discussed.The process conditions of electrochemical etching stainless steel were determined.A clear pattern is quickly etched on the surface of stainless steel,and the etching groove is flat and even silver-white.In the process of etching,the electrolyte and the waste liquid produced are very few,which conforms to the requirements of cleaner production and environmental protection.
引文
[1]秦思楠,樊庆文,刘胜青,等.电化学蚀刻金属零件标记实验研究[J].实验科学与技术,2005(02):67-68.
[2]杨军胜,刘存海.低碳钢蚀刻工艺技术的研究[J].陕西科技大学学报,2012,30(04):46-48.
[3]孙从征,管从胜.不锈钢模具板化学蚀刻、抛光和电镀铬研究[J].电镀与精饰,2006,28(01):14-17.
[4]王希,赵东标,云乃彰.基于电容模型的脉冲电解、电化学光整、蚀刻加工机理分析[J].机械科学与技术,2005,24(12):1449-1451.
[5]万亭.零件电化学蚀刻工艺探析[J].电镀与精饰,2013,35(03):25-27.
[6]李博,李涛.TC18钛合金电化学蚀刻标记新工艺研究[J].电镀与精饰,2018,40(06):14-16.
[7]万亭.零件电化学蚀刻工艺探析[J].电镀与精饰,2013,35(03):25-27.
[8]张丽芬.镁钙锌合金热挤压及电化学蚀刻成形工艺[D].天津大学,2012.
[9]杨涛.电化学蚀刻机床及试验系统的研制[D].合肥工业大学,2012.
[10]李博,李涛.TC18钛合金电化学蚀刻标记新工艺研究[J].电镀与精饰,2018,40(06):14-16.
[11]张波.水溶液中铬电氧化还原过程及铬系材料制备[D].中国科学院大学(中国科学院青海盐湖研究所),2017.
[12]户亚娜.医用微流道模具掩膜电解加工数值模拟及工艺研究[D].大连理工大学,2017.
[13]潘月.静电压微细电解加工技术研究[D].燕山大学,2016.
[14]杭小琳.激光铣削对激光熔覆成形件的整形机理和试验研究[D].苏州大学,2015.
[15]王光燕.DMFC阳极流场超疏水微通道制作及其气泡消减特性研究[D].大连理工大学,2013.
[16]万亭.零件电化学蚀刻工艺探析[J].电镀与精饰,2013,35(03):25-27.
[17]张丽芬.镁钙锌合金热挤压及电化学蚀刻成形工艺[D].天津大学,2012.
[18]杨涛.电化学蚀刻机床及试验系统的研制[D].合肥工业大学,2012.
[19]秦峻.RFID导电油墨的制备与性能研究[D].国防科学技术大学,2011.
[20]余焕权.不锈钢花纹图案蚀刻技术[J].材料保护,2000(02):22-25.
[21]张海岩,沈健.黄铜电化学蚀刻工艺[J].新技术新工艺,1995(04):35.
[22]张海岩,沈健.黄铜电化学蚀刻工艺[J].新技术新工艺,1995(04):35.
[2]杨军胜,刘存海.低碳钢蚀刻工艺技术的研究[J].陕西科技大学学报,2012,30(04):46-48.
[3]孙从征,管从胜.不锈钢模具板化学蚀刻、抛光和电镀铬研究[J].电镀与精饰,2006,28(01):14-17.
[4]王希,赵东标,云乃彰.基于电容模型的脉冲电解、电化学光整、蚀刻加工机理分析[J].机械科学与技术,2005,24(12):1449-1451.
[5]万亭.零件电化学蚀刻工艺探析[J].电镀与精饰,2013,35(03):25-27.
[6]李博,李涛.TC18钛合金电化学蚀刻标记新工艺研究[J].电镀与精饰,2018,40(06):14-16.
[7]万亭.零件电化学蚀刻工艺探析[J].电镀与精饰,2013,35(03):25-27.
[8]张丽芬.镁钙锌合金热挤压及电化学蚀刻成形工艺[D].天津大学,2012.
[9]杨涛.电化学蚀刻机床及试验系统的研制[D].合肥工业大学,2012.
[10]李博,李涛.TC18钛合金电化学蚀刻标记新工艺研究[J].电镀与精饰,2018,40(06):14-16.
[11]张波.水溶液中铬电氧化还原过程及铬系材料制备[D].中国科学院大学(中国科学院青海盐湖研究所),2017.
[12]户亚娜.医用微流道模具掩膜电解加工数值模拟及工艺研究[D].大连理工大学,2017.
[13]潘月.静电压微细电解加工技术研究[D].燕山大学,2016.
[14]杭小琳.激光铣削对激光熔覆成形件的整形机理和试验研究[D].苏州大学,2015.
[15]王光燕.DMFC阳极流场超疏水微通道制作及其气泡消减特性研究[D].大连理工大学,2013.
[16]万亭.零件电化学蚀刻工艺探析[J].电镀与精饰,2013,35(03):25-27.
[17]张丽芬.镁钙锌合金热挤压及电化学蚀刻成形工艺[D].天津大学,2012.
[18]杨涛.电化学蚀刻机床及试验系统的研制[D].合肥工业大学,2012.
[19]秦峻.RFID导电油墨的制备与性能研究[D].国防科学技术大学,2011.
[20]余焕权.不锈钢花纹图案蚀刻技术[J].材料保护,2000(02):22-25.
[21]张海岩,沈健.黄铜电化学蚀刻工艺[J].新技术新工艺,1995(04):35.
[22]张海岩,沈健.黄铜电化学蚀刻工艺[J].新技术新工艺,1995(04):35.