摘要
研究了高强度导磁钢板电磁性能随轧制方向的变化。结果表明,在2 500~15 000A/m直流磁化场范围内,磁性能随轧制偏离角度有显著变化,磁感应强度与纵向偏离角度成非线性关系,最大磁感应强度与轧制方向的偏离角在30~40°之间,横向最小;最大值矫顽力与轧制方向的偏离角为20°,横向最小。造成高强度导磁钢板磁各向异性的主要原因是由于钛和铌的加入对材料晶粒取向改变所致。
The magnetic anisotropy of high strength magnetic steel sheet was studied.The results showed that magnetic properties significantly change with rolling direction and there is a non-linear relationship between magnetic induction and longitudinal deviation angle in 2500~15000A/m DC magnetic field range;the deviation angle between the maximum magnetic induction and rolling direction is from30°to 40°,with the minimum at the transverse direction,while the deviation angle between the maximum coercive force and rolling direction is 20°,with the minimum at the transverse direction.The main cause of this result is that addition of Ti and Nb affects grain orientation.
引文
1施立发,朱涛,王立涛,等.CSP流程生产高磁感无取向电工钢磁各向异性研究.钢铁研究学报,2011,23(4):42-45.
2 石文敏,刘静,郑泽林,等.3.0%Si无取向硅钢磁各向异性的研究.武汉工程职业技术学院学报,2012,24(2):4-7.
3 姚蜡红,冯大军,雷明.硅钢片不同方向0~360°磁性的测试.武汉工程职业技术学院学报,2005,17(4):10-13.
4 董爱锋,苗晓,申毅,等.冷轧压下率对无取向硅钢织构和磁性能的影响.第十届全国电工钢专业学术年会论文集,2008:131-135.
5 何忠治.电工钢.北京:冶金工业出版社,1997:56.
6 徐向棋,金自力.冷轧无取向硅钢的磁晶各向异性能的模拟.特殊钢,2006,27(5):21-23.
7 金自力,任慧平,张红杰.无取向硅钢退火织构的演变与磁性能关系的研究.材料热处理学报,2007,28(2):77-80.