摘要
退火工艺及二次冷轧工艺是生产超薄规格食品级DR材镀锡板的关键控制技术。通过试验对比分析了不同一轧厚度、不同退火目标硬度和不同二次冷轧压下率工艺条件下所得产品的性能指标。认为采用了T3(57HR3OT)硬度退火工艺+26. 20%二次冷轧压下率工艺模式生产0. 14 mm厚的DR9类产品,生产难度小、成本低。同时研究确定了780℃+220 mm/min为生产该类产品的最佳连退工艺。
Annealing process and secondary cold rolling process are the key control technologies for the production of ultra-thin food grade DR tinplate. The property indexes under different rolling thickness,annealing target hardness and secondary cold rolling reduction rate were compared and analyzed through experiments.It is considered that if the DR9 products,with 0. 14 mm thickness,are produced by T3( 57HR3OT)hardness annealing process plus secondary cold rolling reduction process 26. 20%,both of the production difficulty and cost will be lower. At the same time,780 ℃ + 220 mm/min was determined as the best continuous regression process for such products.
引文
[1]刘连喜,刘建兵.中国金属包装产业及包装材料的发展现状及趋势[J].河北冶金,2015,(7):76~78.
[2]张洪波,冯晓勇,李梦英,等.镀锡用二次冷轧材(DR材)的研究进展与应用现状[J].河北冶金,2017,(4):1~5.
[3]孙中华,安治国,熊自柳,等. SPCC薄板冷轧及连续退火工艺研究[J].河北冶金,2013,(2):1~8.
[4]孟德亮,王川仲,海峰,等.冷轧压下率对超低碳深冲钢再结晶退火组织与性能的影响[J].热加工工艺,2016,(5):127~129.
[5]王健,李俊,宓小川.快速加热过程中冷轧钢板的回复和再结晶行为[J].材料热处理学报,2014,(3):101~105.
[6]郭瑞鹏,崔岩,贵永亮.冷变形量对低碳冷轧板组织及再结晶温度的影响[J].钢铁钒钛,2014,(8):122~126.
[7]马胜梅,金自力. CSP冷轧薄板退火过程再结晶机理的研究[J].金属热处理,2012,(6):29~31.
[8]孙开宇,金自力,任慧平,等.再结晶阶段加热速度对低碳冷轧板罩式退火过程组织和织构的影响[J].钢铁研究学报,2014,(5):43~46+53.
[9]潘欣,华维,林瑞民,等.罩式炉退火过程中温度对08Al冷轧钢带再结晶的影响[J].金属热处理,2011,(7):61~63.
[10]胡乐康,陈海军.冷轧钢卷罩式炉再结晶退火延伸率不合格原因分析[J].科技创新导报,2011,(9):47+49.