水性醇酸树脂涂料的改性研究进展
|
摘要
从树脂改性及颜填料改性两方面综述了水性醇酸树脂涂料的改性研究进展,包括引入聚氨酯、苯乙烯、丙烯酸、石墨烯等改性方法,以及颜填料的物理化学改性等,并展望了未来的研究方向。
The modification research progress of waterborne alkyd coatings was reviewed from the aspects of resin modification and pigment filler modification,including the introduction of polyurethane,styrene,acrylic acid,graphene,and other modification methods as well as physical and chemical modification of pigments and fillers. The future research direction were being looked forward to.
The modification research progress of waterborne alkyd coatings was reviewed from the aspects of resin modification and pigment filler modification,including the introduction of polyurethane,styrene,acrylic acid,graphene,and other modification methods as well as physical and chemical modification of pigments and fillers. The future research direction were being looked forward to.
引文
[1] Levine E,Kuzma E J. Polyacrylate-modified Water-borne Alkyds[J]. Journal of Coatings Technology,1998,51(657):35-48.
[2]夏正斌,欧灿斌,张燕红.一种聚氨酯-氨基树脂改性水性醇酸树脂及制备与应用:CN,105153387A[P].2015-12-16.
[3]齐增清.环氧改性水性醇酸树脂的合成与应用[D].广东广州:广东工业大学,2011.
[4]杨振波,杨忠林,郭万生,等.鳞片状富锌涂层耐蚀机理的研究[J].中国涂料,2006,21(1):24-26.
[5] Dhoke S K,Sinha T J M,Khanna A S. Effect of NanoZnO Particles on the Corrosion Behavior of Alkyd-Based Waterborne Coatings[J]. Progress in Organic Coatings,2009,64(4):371-382.
[6]吴翠平,郭永昌,魏晨洁,等.人造石材用重质碳酸钙填料的表面改性研究[J].非金属矿,2016,39(4):21-23.
[7]宋玉强.鳞片状无机填料改性及其对涂层性能的影响[D].江苏南京:南京航空航天大学,2016.
[2]夏正斌,欧灿斌,张燕红.一种聚氨酯-氨基树脂改性水性醇酸树脂及制备与应用:CN,105153387A[P].2015-12-16.
[3]齐增清.环氧改性水性醇酸树脂的合成与应用[D].广东广州:广东工业大学,2011.
[4]杨振波,杨忠林,郭万生,等.鳞片状富锌涂层耐蚀机理的研究[J].中国涂料,2006,21(1):24-26.
[5] Dhoke S K,Sinha T J M,Khanna A S. Effect of NanoZnO Particles on the Corrosion Behavior of Alkyd-Based Waterborne Coatings[J]. Progress in Organic Coatings,2009,64(4):371-382.
[6]吴翠平,郭永昌,魏晨洁,等.人造石材用重质碳酸钙填料的表面改性研究[J].非金属矿,2016,39(4):21-23.
[7]宋玉强.鳞片状无机填料改性及其对涂层性能的影响[D].江苏南京:南京航空航天大学,2016.