摘要
主要对三类玻纤增强聚丙烯材料GFPP-20、GFPP-35、GFPP-50进行研究,通过对挤出工艺、注塑工艺进行特定的优化使得材料力学性能有了明显提高,研究表明挤出速度250 r/min、挤出温度230℃、喂料速度40 r/min、注塑速度80%、注塑压力3 MPa、注塑温度230℃、螺杆背压0 MPa时,玻纤增强聚丙烯的性能最优。测试结果显示,GFPP-20的拉伸强度可达93 MPa、弯曲强度可达125 MPa,GFPP-35的拉伸强度可达123 MPa、弯曲强度可达169 MPa,GFPP-50的拉伸强度可达132 MPa、弯曲强度可达178 MPa。
The effects of extrusion and injection process on the performance of three kinds of short glass fiber filled polypropylene( PP) composites( GFPP-20,GFPP-35 and GFPP-50) were studied. Through the optimization of extrusion and injection process,the mechanical properties had been significantly improved.The study shows that the condition for the optimal performance of short glass fiber filled PP composites is250 RPM extrusion speed,230 ℃ extrusion temperature,40 r/min feed rate,80% injection speed,3 MPa injection pressure,230 ℃ injection temperature and 0 MPa backpressure. The test results indicate that the tensile and flexural strength of GFPP-20,GFPP-35 and GFPP-50 could achieve 93 MPa/125 MPa,123 MPa/169 MPa,and 132 MPa/178 MPa,respectively.
引文
[1]胡友良,乔金梁,吕立新,等.聚烯烃功能化及改性[M].北京:化学工业出版社,2006.
[2]王经武.塑料改性技术[M].北京:化学工业出版社,2004.
[3]邵静波.PP-g-MAH对玻璃纤维增强PP的影响[J].合成树脂及塑料,2006,23(4):5-8.
[4]洪定一.聚丙烯-原理、工艺与技术[M].北京:中国石化出版社,2007.
[5]李正光.聚丙烯生产技术及应用[M].北京:石油工业出版社,2006.
[6]周殿明,张丽珍.聚丙烯成型技术问答[M].北京:化学工业出版社,2007.
[7]张超,徐洪耀,夏建盟,等.长玻璃纤维增强聚丙烯复合材料力学性能研究[J].塑料工业,2017,45(12):78-82.
[8]张超,徐洪耀,夏建盟,等.长玻纤增强PP/PA6合金材料的性能[J].工程塑料应用,2017,45(11):7-12.
[9]韩领,王雄刚,孟凡地,等.GF增强PP复合材料的尺寸稳定性与力学性能[J].工程塑料应用,2017,45(5):24-28.
[10]唐梓健,杨丽庭,李彦涛,等.聚丙烯/玻璃纤维/滑石粉复合材料的制备及性能研究[J].塑料工业,2017,45(1):80-83.
[11]张伟,孙圳,吴玉成.低气味低VOC玻纤增强聚丙烯材料的研制[J].工程塑料应用,2017,45(1):35-38.
[12]黎敏荣,薛平,贾明印,等.纤维增强热塑性树脂复合材料成型技术研究进展[J].塑料工业,2016,44(11):5-10.