摘要
采用国产喷雾热分解设备制备了Bi-2223前驱粉末,分别选用一步收集和分级收集热分解后的粉末,对不同方式收集的粉末进行了XRD分析、SEM观察以及ICP-AES分析,对比了粉末在相成份以及含量、外观形貌、粒径大小和元素原子配比等方面的差别,最终发现采用一步收集方式采集的粉末在相组成、成分均匀度以及原子配比方面均优于分级收集粉末,一步收集方式更适合于收集Bi-2223喷雾热分解粉末.
Bi-2223 precursor powders were fabricated based on the domestic spray pyrolysis equipment.Different powders were collected with different collection methods as one-step and graded collection process.XRD,SEM and ICP-AEC characterizations were performed to study the phase composition,microstructures,as well as the chemical composition of different powders.Based on the obtained results,it was deduced that the powders with one-step collection method exhibited higher uniformity on the phase composition,chemical composition and microstructures,thus would be more suitable for the fabrication of high property Bi-2223 tapes.
引文
[1]周廉,甘子钊等,北京:化学工业出版社,2007:28.
[2]李成山,东北大学博士论文.,(2003),29.
[3]S.A.Halim,S.A.Khawaldeh,S.B.Mohamed,et.al,Materials Chemistry and Physics,61(1999),251.
[4]R.S.Liu,W.N.Wang,C.T.Chang,et.al,Jpn.J.Appl.Phys,28(1989),2155.
[5]C H Jiang,J M Yoo,J W Ko,et.al,Physica C,386(2003),186;Acta Metallurgica Sinica,16(2)(2003),84.
[6]C.Y.Shei,R.S.Liu,C.T.Chang,et.al,Inorg.Chem.,29(1990),3117.
[7]Jaimoo Yoo,Sunghwan Kim,Jae-woong Ko,et.al,Supercond.Sci.Technol.,17(2004),538.
[8]绫井直树,CN200880000805.9,2009-09-30.
[9]畳谷和晃,绫井直树,下山淳一,CN201080039818.4,2012-05-30.
[10]S.Kobayashi,T.Kato,K.Yamazaki,et.al,IEEE TRANSACTIONS ON APPLIED SUPERCONDUCTIVITY,15(2)(2005),2534.