摘要
研究了钠盐三元变质剂的加入量对ZL101合金变质过冷度和变质时间的影响。试验结果表明:在所建立的钠盐三元变质剂加入量、变质处理过冷度和变质时间三者的准三维图上,可以直接获得合金在最佳变质效果时(变质处理凝固时过冷度最大),钠盐加入量与变质时间的对应关系;也可以获得合金在具有变质效果时(变质处理凝固时过冷度大于4℃),钠盐加入量与变质时间的对应关系。
This research focused primarily on studying the effect of different amounts of ternary sodium salt modifier on the super-cooling and modification time during metamorphic treatment of ZL101 alloy. A quasi-threedimensional curved surface diagram was established based on the addition amount of sodium salt modifier,metamorphic treatment super-cooling degree and modification time, in which the relationship between the addition amount of sodium salt and the modification time upon appearing the optimal metamorphic effect(the maximum super-cooling degree during the modification of solidification treatment), and upon appearing the metamorphic effect(when super-cooling degree is more than 4℃ during the setting treatment), could be directly obtained.
引文
[1]Sun Yu,Pang S P,Liu X R,et al. Nucleation and growth of eutectic cell in hypoeutectic Al-Si alloy[J]. Transactions of Nonferrous Metals Society of China,2011,21(10):2186-2191.
[2]王文华,司乃潮,刘光磊,等.热处理工艺对多元Al-Si合金力学性能的影响[J].铸造,2012,61(8):925-928.
[3]马广辉,李润霞,段林.铸造缺陷对ZL101合金断裂行为的影响[J].铸造,2018,67(2):162-166.
[4]李豹,张志峰,王志刚,等. Sr对铸态Al-7Si-Mg合金组织和力学性能的影响[J].特种铸造及有色合金,2013,33(8):691-694.
[5]宋丽英,刘昊昕,聂赛男,等. Sr变质对ZL101合金显微组织和低温拉伸性能的影响[J].铸造,2018,67(2):146-151.
[6]董光明,廖恒成,孙国雄,等. Sb变质后Al-Si合金共晶组织的不均匀性[J].特种铸造及有色合金,2011,31(5):418-420.
[7]胡中潮,于慧,崔元胜,等. Sb、Te变质对ZL101合金组织和性能的影响[J].铸造,2018,67(6):502-506.
[8]赵光伟,丁翀,叶喜葱,等. Al-Cu-Mg包共晶合金凝固组织演变及凝固路径研究[J].铸造,2018(3):203-207.
[9]吕孟杰,陈建勋,吴树森,等.锑对铝硅合金变质效果的炉前快速热分析研究[J].铸造,2017,66(1):11-15.