摘要
福建某金精矿焙砂主要组成矿物为赤铁矿与石英,金、银含量分别为31.27 g/t、824 g/t。采用自主合成的嗜金1号药剂从稀硫酸脱铜后的该金精矿焙砂中提取金、银。结果表明,在嗜金1号用量为5 g/L、pH为11、液固比为5 mL/g、浸出温度为25℃、浸出时间为24 h时,金与银的浸出率分别达到92.76%、85.02%。比以氰化钠为浸出剂时,金浸出率提高了3.73个百分点。嗜金1号的浸金效果较优,且嗜金1号较氰化钠对环境的影响较弱。因此,嗜金1号可以用于含金焙砂的金浸出工艺。
The main phase of the gold concentrate calcine in Fujian Province is hematite and quartz. The content of gold and silver is 31.27 g/t and 824 g/t,respectively. The copper was extracted by dilute sulfate leaching method. Then,the gold and silver were extracted by the self-made agent named Addicted-gold NO.1. The result showed that when the Addicted-gold NO.1 agent dosage of 5 g/L,p H value of 11,liquid-to-solid ratio of 5 mL/g,reaction temperature of 25 ℃,leaching time of 24 h,leaching rate of gold and silver were 92.76% and 85.02%,respectively. The leaching rate of gold was 3.73 percentage points higher than that by sodium cyanide method. Hence,the Addicted-gold NO.1 not only has excellent effect of the gold leaching rate,but also has weak impact on the environment. Therefore,the Addicted-gold NO.1 can be used in gold leaching process from gold concentrate calcine.
引文
[1]谢建宏,贾学国,张晓民.黄金选冶[M].北京:冶金工业出版社,2014.Xie Jianhong,Jia Xueguo,Zhang Xiaomin.Gold Ore Processing[M].Beijing:Metallurgy Industry Press,2014.
[2]陆春雷,陈明,左锐.危化品运输当警钟长鸣--三起交通事故引发氰化钠污染案的启示[J].环境保护,2011(9):40-42.Lu Chunlei,Chen Ming,Zuo Rui.The alarm bell all the time-enlightenment caused by three sodium cyanide pollution caused by traffic accidents[J].Environmental Protection,2011(9):40-42.
[3]何超然,丁冲,王晓辉,等.氰化尾渣碱法水热浸出脱石英试验[J].金属矿山,2018(3):192-195.He Chaoran,Ding Chong,Wang Xiaohui,et al.Research on desilicication of cyanide tailings via alkaline hydrothermal process[J].Metal Mine,2018(3):192-195.
[4]党晓娥,王璐,孟裕松,等.某环保药剂的浸金性能及贵液中金的活性炭吸附特性[J].黄金科学技术,2017(6):114-120.Dang Xiaoe,Wang Lu,Meng Yusong,et al.Performance of an environmental gold leaching agent and activated carbon adsorption characteristics of gold in the liquid[J].Gold Science and Technology,2017(6):114-120.
[5]刘宪超,蒋中刚,唐道文,等.难浸金矿石的次氯酸钠浸出试验研究[J].湿法冶金,2014,33(6):413-415.Liu Xianchao,Jiang Zhonggang,Tang Daowen,et al.Experimental study on leaching of gold from a refractory gold ore using sodium hypochlorite[J].Hydrometallurgy of China,2014,33(6):413-415.
[6]史娟华,于先进,张亚莉,等.氯化钠-次氯酸钠法从氰化渣中回收金[J].有色金属:冶炼部分,2013(3):35-37.Shi Juanhua,Yu Xianjin,Zhang Yali,et al.Sodium chloride-sodium hychlorite method for gold recovery from cyanide residue[J].Nonferrous Metals:Extractive Metallurgy,2013(3):35-37.
[7]刘家弟,刘凤春.难浸金精矿硫脲浸金试验研究[J].矿业研究与开发,2017(9):36-39.Liu Jiadi,Liu Fengchun.Experimental study on gold leaching from refractory gold concentrate by thiourea[J].Mining Research and Development,2017(9):36-39.
[8]马方通,高利坤,董方,等.硫脲浸金及置换法从硫脲溶液中回收金研究现状[J].湿法冶金,2017,36(4):257-261.Ma Fangtong,Gao Likun,Dong Fang,et al.Situations of leaching and replacement of gold in acidic thiourea solution[J].Hydrometallurgy,2017,36(4):257-261.
[9]吴浩,黄万抚,邱峰,等.硫氰酸盐浸金研究进展[J].贵金属,2016,37(3):72-78.Wu Hao,Huang Wanfu,Qiu Feng,et al.Review of gold leaching by thiocyanate[J].Precious Metals,2016,37(3):72-78.
[10]Ma C J,Li J Y,Liu R J.A review of thiocyanate hydrometallurgy for the recovery of gold[J].Applied Mechanics&Materials,2015,68(s):53-61.
[11]Mohammadi E,Pourabdoli M,Ghobeiti Hasab M,et al.Ammoniacal thiosulfate leaching of refractory oxide gold ore[J].International Journal of Mineral Processing,2017(4):6-10.
[12]刘有才,朱忠泗,符剑刚,等.某金矿石的石硫加碱催化合剂法浸金研究[J].稀有金属,2013,37(1):123-129.Liu Youcai,Zhu Zhongsi,Fu Jiangang,et al.Leaching and gold ores by lime-sulphur-synthetic-solution with alkali-catalyzed process[J].Chinese Journal of Rare Metals,2013,37(1):123-129.