再生骨料混凝土抗冻性研究进展
|
摘要
随着建筑业的发展,大量建筑垃圾的产生和处理催生了再生混凝土的研究应用和发展。在我国北方广大地区以及华中南部分地区的建筑物都不同程度的遭受到冻融循环作用的影响。开展再生混凝土抗冻性能研究具有重要意义。鉴于此,大量查阅了近年来关于再生混凝土抗冻耐久性研究的相关文献,系统总结并分析了再生混凝土冻融破坏机理、抗冻耐久性影响因素及主要措施。在此基础之上,结合当下的研究现状提出了未来的研究方向,旨在丰富和发展再生混凝土的理论研究,推动再生混凝土的工程应用。
With the development of the construction industry,a large amount of construction rubbish generation and treatment has given birth to the research and development of recycled concrete.In many parts of northern China and parts of central and southern China,buildings are affected to varying degrees by the freeze-thaw cycle.Promoting the research on the frost resistance of recycled concrete is of great significance.Therefore,lots of related literatures about the research on the freeze-thaw durability of recycled concrete are reviewed.The mechanism of freeze-thaw failure of recycled concrete,the influencing factors of freeze-thaw durability and the main measures are systematically analyzed.On this basis,this paper puts forward the future research direction according to the current research status,aiming to enrich and develop the theoretical research of recycled concrete and promoting the engineering application of recycled concrete
With the development of the construction industry,a large amount of construction rubbish generation and treatment has given birth to the research and development of recycled concrete.In many parts of northern China and parts of central and southern China,buildings are affected to varying degrees by the freeze-thaw cycle.Promoting the research on the frost resistance of recycled concrete is of great significance.Therefore,lots of related literatures about the research on the freeze-thaw durability of recycled concrete are reviewed.The mechanism of freeze-thaw failure of recycled concrete,the influencing factors of freeze-thaw durability and the main measures are systematically analyzed.On this basis,this paper puts forward the future research direction according to the current research status,aiming to enrich and develop the theoretical research of recycled concrete and promoting the engineering application of recycled concrete
引文
[1]韦庆东,孙俊,黄沛增,等.再生骨料对混凝土的抗氯离子渗透性能影响[J].混凝土,2014(12):101-104.
[2]余乃宗,刘卫东,陈冲.再生细骨料砂浆配合比优化分析[J].混凝土,2015(9):116-118.
[3]THOMASC,SETINJ,POLANCOJA,et al.Durability of recycled aggregate concrete[J].Construction and Building Materials,2013(40):1054-1065.
[4]李秋义,全洪珠,秦原.混凝土再生骨料[M].北京:中国建筑工业出版社,2011.
[5]崔素萍,杜鑫,兰明章,等.不同矿物掺和料对再生细骨料混凝土耐久性影响的研究[J].混凝土世界,2011(2):82-85.
[6]GOKCE A,NAGATAKI S,SAEKI T,et al.Freezing and thawing resistance of air-entrained concrete incorporating recycled coarse aggregate:the role of air content in demolished concrete[J].Cementand Concrete Research,2004,34(5):799-806.
[7]陈爱玖,章青,王静,等.再生混凝土冻融循环试验与损伤模型研究[J].工程力学,2009(11):102-107.
[8]王怀亮,张楠.改性再生骨料对自密实混凝土性能的影响[J].哈尔滨工业大学学报,2016(6):150-156.
[9]混凝土用再生粗骨料:GB/T 25177-2010[S].
[10]韩帅,李秋义,张修勤,等.再生粗骨料品质和取代率对再生混凝土抗冻性能影响[J].中国海洋大学学报(自然科学版),2017(1):96-104.
[11]曹剑.再生粗骨料品质和取代率对再生混凝土抗冻性能的影响[J].青岛理工大学学报,2016(4):17-20.
[12]陶桂东,蒋开东,张劲松,等.III类再生骨料对C60混凝土性能影响的研究[J].工程质量,2015(4):39-43.
[13]李飞,张晓奇,董汇标,等.再生废砖粗骨料对混凝土性能的影响[J].混凝土,2015(2):56-58.
[14]汤贝贝,王磊,宗兰,等.碎砖骨料再生混凝土的抗冻性能试验研究[J].江苏建材,2015(3):26-29.
[15]舒倩,姜新佩,董云婷.富含砖粒再生骨料混凝土的耐久性试验研究[J].河北工程大学学报(自然科学版),2017(1):43-47.
[16]王佳骅,王功勋,黄丹,等.废瓷砖再生骨料混凝土的配制及性能试验研究[J].硅酸盐通报,2014(1):3000-3005.
[17]王磊,孙勇.再生陶瓷骨料混凝土冻融性能研究[J].低温建筑技术,2016(6):6-8.
[18]王玲玲,陈彦文,潘文浩,等.制备工艺对再生混凝土耐久性影响研究[J].混凝土,2012(11):142-144.
[19]SALLEHANI,MAHYUDDINR.Engineering properties of treated recycled concrete aggregate(RCA)for structura lapplications[J].Construction and Building Materials,2013(44):464-476.
[20]杨飞华,郝利炜,程海丽.水玻璃改性废混凝土再生粗骨料对混凝土强度及抗冻性影响试验.
[21]陈建良,倪竹萍.强化处理改善再生骨料混凝土性能试验[J].低温建筑技术,2011(2):14-16.
[22]陈彦文,潘文浩,孙小巍.预处理再生骨料混凝土性能的试验研究[J].混凝土,2012(1):81-83.
[23]李滢,代大虎,余红发.再生骨料强化技术对再生混凝土性能影响研究[J].青海大学学报(自然科学版),2016(2):1-4.
[24]余乃宗,刘卫东,欧阳瑞,等.再生细骨料对混凝土力学性能及抗冻性能研究[J].水利与建筑工程学报,2016(4):117-122.
[25]李滢,代大虎,余红发.再生细骨料对再生混凝土力学性能及耐久性能的影响研究[J].混凝土,2016(12):76-78.
[26]崔素萍,杜鑫,兰明章,等.不同矿物掺和料对再生细骨料混凝土耐久性影响的研究[J].混凝土世界,2011(2):82-85.
[27]李卫宁.再生骨料取代率对再生混凝土路面抗冻性的影响研究[J].西部交通科技,2017(10):1-3.
[28]ABBAS A,FATHIFAZL G,ISGOR O B,et al.Durability of recycled aggregate concrete designed with equivalent mortar volume method[J].Cement and Concrete Composites,2009,31(8):555-563
[29]周宇,郑秀梅,李广军,等.再生骨料混凝土抗冻性能试验研究[J].低温建筑技.
[30]谢静静,朱平华.基于抗冻性的混凝土再生粗骨料最优取代率试验研究[J].建筑结构,2016(2):35-38.
[31]冯嘉,李秋义,宋菁,等.再生粗骨料混凝土抗冻性试验研究[J].青岛理工大学学报,2011(4):44-48.
[32]魏成娟,高辉,薛鹏飞,等.再生骨料混凝土耐久性试验研究[J].施工技术,2015(S2):486-488.
[33]刘发明,刘飞,朱陈陈.废弃混凝土试块掺合型再生混凝土抗冻性试验研究[J].长春工程学院学报(自然科学版),2017(2):14-18.
[34]陈爱玖,陈萌,王静,等.玄武岩纤维对橡胶再生混凝土抗冻性能的影响[J].混凝土,2016(5):62-65.
[35]汪振双,王宝民,苏昊林,等.橡胶颗粒对再生混凝土耐久性影响[J].哈尔滨工业大学学报,2015(6):109-112.
[36]杨洪生,王帅,赵庆新.橡胶粉改性再生骨料混凝土抗冻性研究[J].土木建筑与环境工程,2012(S1):130-134.
[37]范鹏飞.橡胶再生混凝土抗冻性能试验研究[J].公路,2015(5):187-190.
[38]张浩博,任慧超,寇佳亮.粉煤灰对再生混凝土抗压及耐久性试验研究[J].西安理工大学学报,2016(4):410-415.
[39]李兵,蒋玲健,王明,等.粉煤灰掺量对再生混凝土性能的影响[J].粉煤灰,2011(3):7-8,11.
[40]朱涛,吴相豪,袁潘.掺石灰粉对粉煤灰再生混凝土抗冻性能的影响[J].粉煤灰,2013(1):40-42.
[41]刘立,赵顺增,曹淑萍,等.高性能再生集料混凝土的耐久性研究[J].粉煤灰,2011(3):29-33.
[42]尹兴伟,吴相豪.矿物掺合料对再生混凝土抗冻性影响的试验研究[J].混凝土,2012(8):90-93.
[43]吴瑾炎,李碧雄,王燕鹏,等.添加粉煤灰和硅粉的路面高性能再生混凝土冻融特性试验研究[J].混凝土,2014(4):66-69.
[44]冯嘉,李秋义,宋菁,等.再生粗骨料混凝土抗冻性试验研究[J].青岛理工大学学报,2011(4):44-48.
[45]伍君勇,朱平华.再生混凝土抗冻性研究进展[J].混凝土,2013(4):15-19.
[46]ZAHARIEVA R,BUYLE-BODIN F,WIRQUIN E.Frost resistance of recycled aggregate concrete[J].Cement and Concrete Research,2004,34(2):1927-1932.
[47]SALEM R M,BURDENTTE E G,JACSON N M.Resistance to freezing and thawing of recycled aggregate concrete[J].ACI Materials Journal,2003,100(3):216-221.
[48]OLIVEIRA M B,VAZQUEZ E.The influence of retained moisture in aggregates from recycling on the properties of new hardened concrete[J].Waste Management,1996,16(1):113-117.
[49]吴中伟,廉惠珍.高性能混凝土[M].北京:中国铁道出版社,1999.
[50]KUMAR R,BHATTACHARJEE B.Porosity,pore size distributionand in situ strength of concrete[J].Cement and Concrete Research,2003,33(2):155-164.
[51]刘庆涛,岑国平,蔡良才,等.机场道面再生混凝土的性能与应用[J].中南大学学报(自然科学版),2012,43(8):3263-3269.
[52]陈爱玖,孙晓培,张敏,等.活性掺合料再生混凝土抗冻性能试验[J].混凝土,2014(6):20-23.
[53]陈爱玖,王静,杨粉,等.纤维再生混凝土的抗冻性能试验研究[J].混凝土,2013(2):1-4.
[54]任磊,赵洪林,袁书成,等.玄武岩纤维增强再生混凝土冻融后基本力学性能试验研究[J].混凝土,2017(8):46-51.
[55]王丽丹,周志云,叶林飞,等.复合微粉和聚丙烯纤维对再生混凝土抗冻性研究[J].上海理工大学学报,2017(3):301-306.
[2]余乃宗,刘卫东,陈冲.再生细骨料砂浆配合比优化分析[J].混凝土,2015(9):116-118.
[3]THOMASC,SETINJ,POLANCOJA,et al.Durability of recycled aggregate concrete[J].Construction and Building Materials,2013(40):1054-1065.
[4]李秋义,全洪珠,秦原.混凝土再生骨料[M].北京:中国建筑工业出版社,2011.
[5]崔素萍,杜鑫,兰明章,等.不同矿物掺和料对再生细骨料混凝土耐久性影响的研究[J].混凝土世界,2011(2):82-85.
[6]GOKCE A,NAGATAKI S,SAEKI T,et al.Freezing and thawing resistance of air-entrained concrete incorporating recycled coarse aggregate:the role of air content in demolished concrete[J].Cementand Concrete Research,2004,34(5):799-806.
[7]陈爱玖,章青,王静,等.再生混凝土冻融循环试验与损伤模型研究[J].工程力学,2009(11):102-107.
[8]王怀亮,张楠.改性再生骨料对自密实混凝土性能的影响[J].哈尔滨工业大学学报,2016(6):150-156.
[9]混凝土用再生粗骨料:GB/T 25177-2010[S].
[10]韩帅,李秋义,张修勤,等.再生粗骨料品质和取代率对再生混凝土抗冻性能影响[J].中国海洋大学学报(自然科学版),2017(1):96-104.
[11]曹剑.再生粗骨料品质和取代率对再生混凝土抗冻性能的影响[J].青岛理工大学学报,2016(4):17-20.
[12]陶桂东,蒋开东,张劲松,等.III类再生骨料对C60混凝土性能影响的研究[J].工程质量,2015(4):39-43.
[13]李飞,张晓奇,董汇标,等.再生废砖粗骨料对混凝土性能的影响[J].混凝土,2015(2):56-58.
[14]汤贝贝,王磊,宗兰,等.碎砖骨料再生混凝土的抗冻性能试验研究[J].江苏建材,2015(3):26-29.
[15]舒倩,姜新佩,董云婷.富含砖粒再生骨料混凝土的耐久性试验研究[J].河北工程大学学报(自然科学版),2017(1):43-47.
[16]王佳骅,王功勋,黄丹,等.废瓷砖再生骨料混凝土的配制及性能试验研究[J].硅酸盐通报,2014(1):3000-3005.
[17]王磊,孙勇.再生陶瓷骨料混凝土冻融性能研究[J].低温建筑技术,2016(6):6-8.
[18]王玲玲,陈彦文,潘文浩,等.制备工艺对再生混凝土耐久性影响研究[J].混凝土,2012(11):142-144.
[19]SALLEHANI,MAHYUDDINR.Engineering properties of treated recycled concrete aggregate(RCA)for structura lapplications[J].Construction and Building Materials,2013(44):464-476.
[20]杨飞华,郝利炜,程海丽.水玻璃改性废混凝土再生粗骨料对混凝土强度及抗冻性影响试验.
[21]陈建良,倪竹萍.强化处理改善再生骨料混凝土性能试验[J].低温建筑技术,2011(2):14-16.
[22]陈彦文,潘文浩,孙小巍.预处理再生骨料混凝土性能的试验研究[J].混凝土,2012(1):81-83.
[23]李滢,代大虎,余红发.再生骨料强化技术对再生混凝土性能影响研究[J].青海大学学报(自然科学版),2016(2):1-4.
[24]余乃宗,刘卫东,欧阳瑞,等.再生细骨料对混凝土力学性能及抗冻性能研究[J].水利与建筑工程学报,2016(4):117-122.
[25]李滢,代大虎,余红发.再生细骨料对再生混凝土力学性能及耐久性能的影响研究[J].混凝土,2016(12):76-78.
[26]崔素萍,杜鑫,兰明章,等.不同矿物掺和料对再生细骨料混凝土耐久性影响的研究[J].混凝土世界,2011(2):82-85.
[27]李卫宁.再生骨料取代率对再生混凝土路面抗冻性的影响研究[J].西部交通科技,2017(10):1-3.
[28]ABBAS A,FATHIFAZL G,ISGOR O B,et al.Durability of recycled aggregate concrete designed with equivalent mortar volume method[J].Cement and Concrete Composites,2009,31(8):555-563
[29]周宇,郑秀梅,李广军,等.再生骨料混凝土抗冻性能试验研究[J].低温建筑技.
[30]谢静静,朱平华.基于抗冻性的混凝土再生粗骨料最优取代率试验研究[J].建筑结构,2016(2):35-38.
[31]冯嘉,李秋义,宋菁,等.再生粗骨料混凝土抗冻性试验研究[J].青岛理工大学学报,2011(4):44-48.
[32]魏成娟,高辉,薛鹏飞,等.再生骨料混凝土耐久性试验研究[J].施工技术,2015(S2):486-488.
[33]刘发明,刘飞,朱陈陈.废弃混凝土试块掺合型再生混凝土抗冻性试验研究[J].长春工程学院学报(自然科学版),2017(2):14-18.
[34]陈爱玖,陈萌,王静,等.玄武岩纤维对橡胶再生混凝土抗冻性能的影响[J].混凝土,2016(5):62-65.
[35]汪振双,王宝民,苏昊林,等.橡胶颗粒对再生混凝土耐久性影响[J].哈尔滨工业大学学报,2015(6):109-112.
[36]杨洪生,王帅,赵庆新.橡胶粉改性再生骨料混凝土抗冻性研究[J].土木建筑与环境工程,2012(S1):130-134.
[37]范鹏飞.橡胶再生混凝土抗冻性能试验研究[J].公路,2015(5):187-190.
[38]张浩博,任慧超,寇佳亮.粉煤灰对再生混凝土抗压及耐久性试验研究[J].西安理工大学学报,2016(4):410-415.
[39]李兵,蒋玲健,王明,等.粉煤灰掺量对再生混凝土性能的影响[J].粉煤灰,2011(3):7-8,11.
[40]朱涛,吴相豪,袁潘.掺石灰粉对粉煤灰再生混凝土抗冻性能的影响[J].粉煤灰,2013(1):40-42.
[41]刘立,赵顺增,曹淑萍,等.高性能再生集料混凝土的耐久性研究[J].粉煤灰,2011(3):29-33.
[42]尹兴伟,吴相豪.矿物掺合料对再生混凝土抗冻性影响的试验研究[J].混凝土,2012(8):90-93.
[43]吴瑾炎,李碧雄,王燕鹏,等.添加粉煤灰和硅粉的路面高性能再生混凝土冻融特性试验研究[J].混凝土,2014(4):66-69.
[44]冯嘉,李秋义,宋菁,等.再生粗骨料混凝土抗冻性试验研究[J].青岛理工大学学报,2011(4):44-48.
[45]伍君勇,朱平华.再生混凝土抗冻性研究进展[J].混凝土,2013(4):15-19.
[46]ZAHARIEVA R,BUYLE-BODIN F,WIRQUIN E.Frost resistance of recycled aggregate concrete[J].Cement and Concrete Research,2004,34(2):1927-1932.
[47]SALEM R M,BURDENTTE E G,JACSON N M.Resistance to freezing and thawing of recycled aggregate concrete[J].ACI Materials Journal,2003,100(3):216-221.
[48]OLIVEIRA M B,VAZQUEZ E.The influence of retained moisture in aggregates from recycling on the properties of new hardened concrete[J].Waste Management,1996,16(1):113-117.
[49]吴中伟,廉惠珍.高性能混凝土[M].北京:中国铁道出版社,1999.
[50]KUMAR R,BHATTACHARJEE B.Porosity,pore size distributionand in situ strength of concrete[J].Cement and Concrete Research,2003,33(2):155-164.
[51]刘庆涛,岑国平,蔡良才,等.机场道面再生混凝土的性能与应用[J].中南大学学报(自然科学版),2012,43(8):3263-3269.
[52]陈爱玖,孙晓培,张敏,等.活性掺合料再生混凝土抗冻性能试验[J].混凝土,2014(6):20-23.
[53]陈爱玖,王静,杨粉,等.纤维再生混凝土的抗冻性能试验研究[J].混凝土,2013(2):1-4.
[54]任磊,赵洪林,袁书成,等.玄武岩纤维增强再生混凝土冻融后基本力学性能试验研究[J].混凝土,2017(8):46-51.
[55]王丽丹,周志云,叶林飞,等.复合微粉和聚丙烯纤维对再生混凝土抗冻性研究[J].上海理工大学学报,2017(3):301-306.