描述了一次硫酸盐三价铬镀黑铬中镍杂质含量超过工艺上限时,高电流密度区镀层出现粗糙故障的排除过程。用二乙基二硫代氨基甲酸钠螯合沉淀法或电解法去除镍杂质后补加发黑剂,镀液恢复正常。
A problem of rough coating formation in high current density area caused by the exceeding of nickel impurities content during trivalent black chromium electroplating in sulfate electrolyte and the corresponding treatment method were described. It was solved by removing nickel impurities via precipitation with sodium dimethyldithiocarbamate, a chelating agent, or via low-current electrolysis, and replenishing the blackening agent.
引文
[1]黄恩礼.三价铬电解液电镀黑铬工艺及市场现状[J].电镀与精饰,2010,32(9):25-26,30.
[2]郭崇武,赖奂汶.一种硫酸盐三价铬电镀黑铬工艺的应用[J].电镀与精饰,2013,35(5):9-11.
[3]郭崇武.硫酸盐三价铬滚镀黑铬工艺研究[J].电镀与涂饰,2014,33(13):565-568.
[4]郭崇武,赖奂汶.硫酸盐体系三价铬常温电镀黑铬工艺[J].电镀与涂饰,2012,31(7):9-11.
[5]郭崇武,易胜飞.金属杂质对三价铬镀铬的影响及处理[J].电镀与精饰,2008,30(9):28-30.
[6]郭崇武.三价铬镀液中三价铬的快速分析[J].电镀与精饰,2009,31(1):41-43.
[7]郭崇武.不含铵盐的三价铬镀液中硼酸的分析[J].电镀与精饰,2012,34(9):37-38.
[8]郭崇武,易胜飞,李健强.三价铬镀铬溶液中六价铬杂质的测定[J].电镀与精饰,2008,30(1):41-43.
[9]郭崇武,易胜飞.三价铬镀液中铁杂质的分析[J].电镀与精饰,2008,30(2):40-42.
[10]郭崇武,易胜飞.三价铬镀液中镍杂质的分析[J].电镀与精饰,2008,30(4):40-42.
[11]郭崇武,易胜飞.三价铬镀液中铜杂质的分析[J].电镀与精饰,2008,30(6):34-36.
[12]郭崇武,李小花.螯合沉淀法去除三价铬镀铬液中的镍和铜杂质[J].电镀与涂饰,2018,37(7):321-322.
[13]郭崇武,赖奂汶.硫酸盐体系快速镀三价铬工艺[J].电镀与涂饰,2011,30(10):13-16.