通过自行开发的电渣重熔连续定向凝固技术(ESR-CDS)成功制备了Φ105mm高纯净、低偏析的定向凝固FGH96合金坯锭,利用等温锻造设备沿平行于柱状晶方向锻压,变形量超过80%,经热处理后得到具有均匀等轴晶组织的饼坯件,晶粒度达到ASTM6级,饼坯件的各种性能均达到粉末冶金FGH96合金锻件的性能要求。
High purity and low segregation directionally solidified FGH96 superalloy ingot(φ160mm and φ105mm) were successfully produced by electroslag remelting continuous directional solidification(ESR-CDS) technology. The ESR-CDS FGH96 superalloy ingots were forged by isothermal forging(IF) technology, strain quantity over 80%. The pancakes got fully recrystallized structure(uniform grain size 40μm) after heat treatment.
引文
[1]Roger C.Reed.The Superalloys:Fundamentals and Applications[M].Cambridge university press,2006:229.
[2]付锐,陈希春,任昊,冯涤.电渣重熔连续定向凝固Rene88DT合金的组织与热变形行为[J],航空材料学报,2011,31(3):8-13.
[3]冯涤,付锐,陈希春,任昊.真空/气体保护电渣重熔连续定向凝固装置与方法:中国,201010614036.0[P].2010-12-1.
[4]付锐.电渣重熔连续定向凝固工艺和技术研究[R],博士后研究工作报告.北京:钢铁研究总院,2011.
[5]D.D.Krueger,R.D.Kissinger,R.D.Menzies.Superalloys1992[C],S.D.Antolovich et al Editors,TMS-AIME,Warrendale PA,(1992),277.
[6]S.T.Wlodek,M.Kelly,D.A.Alden.[C],Superalloys 1996[C],R.D.Kissinger et al Editors,TMS-AIME,Warrendale PA,(1996),129.
[7]D.D.Krueger,R.D.Kissinger,R.D.Menzies,C.S.Wukusick.US,4957567[P].1990-9-18.