脱硫石膏品质控制及资源化利用
|
摘要
脱硫石膏是燃煤电厂湿法脱硫工艺产生的固体废物。通过对电厂脱硫石膏品质检测,分析电厂脱硫系统对脱硫石膏品质的主要影响因素,提出针对性的品质改善措施,并为脱硫石膏资源化利用提供应用途径。
Flue gas desulphurization(FGD) gypsum is the byproduct produced in the purification treatment of flue gas in coal-fired power plants. By detecting the FGD gypsum quality and analyzing the main influencing factors of desulfurization system on the desulfurization gypsum quality,specific quality improvement measures are put forward. The comprehensive application of desulfurization gypsum is also provided.
Flue gas desulphurization(FGD) gypsum is the byproduct produced in the purification treatment of flue gas in coal-fired power plants. By detecting the FGD gypsum quality and analyzing the main influencing factors of desulfurization system on the desulfurization gypsum quality,specific quality improvement measures are put forward. The comprehensive application of desulfurization gypsum is also provided.
引文
[1]洪燕.我国脱硫石膏综合利用分析及建议[J].中国资源综合利用,2013(9):42-43.
[2]丛钢,邢世健,张沪.脱硫石膏性能研究[J].新型建筑材料,1997(12):10-12.
[3]刘涛,薛建明,王小明,等.湿法烟气脱硫石膏资源化深度利用[J].中国电力,2009(8):65-69.
[4]Tzouvalas G,Rantis G,Tsimas S.Alternative calcium-sul fatebearing materials as cement retarders:Part II.FGD gypsum[J].Cement and concrete research,2004,34(11):2119-2125.
[5]Valimbe P S,Malhotra V M.Effects of water content and temperature on the crystallization behavior of FGD scrubber sludge[J].Fuel,2002,81(10):1297-1304.
[6]孙令文,赵建华.电厂烟气脱硫副产物石膏的循环利用[J].电力环境保护,2008(4):29-31.
[7]王瑾,杨剑,赵良庆,等.脱硫石膏的综合利用现状[J].环境工程,2012(S2):467-469.
[8]章明朗.脱硫石灰石微粉生产工艺分析[J].水泥科技,2006(1):37-38.
[9]王五清,贺元启.石灰石/石膏湿法烟气脱硫工艺与关键参数分析[J].华北电力技术,2004(2):1-2.
[10]纪立国.石灰石-石膏湿法烟气脱硫工艺系统研究及其优化[D].北京:华北电力大学,2001
[11]林少敏,黄利榆,陈少瑾.氯离子对脱硫石膏结晶性能的影响[J].广东化工,2010,37(7):17-18.
[12]钟毅,林永明,高翔,等.石灰石/石膏湿法烟气脱硫系统石灰石活性影响因素研究[J].电站系统工程,2005,21(4):2-4.
[13]方婷,官民鹏.影响湿法脱硫石膏脱水效率的因素研究[J].北方环境,2011(7):186-187.
[14]丛钢,龚七一,丁宇.脱硫石膏作水泥缓凝剂研究[J].水泥,1997(3):6-8.
[15]胥桂萍,童仕唐.从FGD残渣制备α型半水石膏过程晶形的控制[J].吉林化工学院学报,2002,19(2):3-7.
[16]Singh N B,Middendorf B.Calcium sulphate hemihydrate hydration leading to gypsum crystallization[J].Progress in Crystal Growth and Characterization of Materials,2007,53(1):57-77.
[17]朱海霞.石膏基自流平砂浆的技术进展研究[J].新型建筑材料,2016(6):1-5.
[18]王舒州,陈德玉,何玉龙,等.磷石膏制备硫酸钙晶须及其应用的研究[J].新型建筑材料,2016,43(3):5-9.
[19]吴蓉.脱硫石膏-秸秆-聚苯颗粒新型墙板的试验研究[J].新型建筑材料,2016,43(7):97-99.
[20]吴敏,施惠生.矿渣及脱硫石膏-粉煤灰复合胶凝材料的试验研究[J].水泥,2008(2):1-6.
[2]丛钢,邢世健,张沪.脱硫石膏性能研究[J].新型建筑材料,1997(12):10-12.
[3]刘涛,薛建明,王小明,等.湿法烟气脱硫石膏资源化深度利用[J].中国电力,2009(8):65-69.
[4]Tzouvalas G,Rantis G,Tsimas S.Alternative calcium-sul fatebearing materials as cement retarders:Part II.FGD gypsum[J].Cement and concrete research,2004,34(11):2119-2125.
[5]Valimbe P S,Malhotra V M.Effects of water content and temperature on the crystallization behavior of FGD scrubber sludge[J].Fuel,2002,81(10):1297-1304.
[6]孙令文,赵建华.电厂烟气脱硫副产物石膏的循环利用[J].电力环境保护,2008(4):29-31.
[7]王瑾,杨剑,赵良庆,等.脱硫石膏的综合利用现状[J].环境工程,2012(S2):467-469.
[8]章明朗.脱硫石灰石微粉生产工艺分析[J].水泥科技,2006(1):37-38.
[9]王五清,贺元启.石灰石/石膏湿法烟气脱硫工艺与关键参数分析[J].华北电力技术,2004(2):1-2.
[10]纪立国.石灰石-石膏湿法烟气脱硫工艺系统研究及其优化[D].北京:华北电力大学,2001
[11]林少敏,黄利榆,陈少瑾.氯离子对脱硫石膏结晶性能的影响[J].广东化工,2010,37(7):17-18.
[12]钟毅,林永明,高翔,等.石灰石/石膏湿法烟气脱硫系统石灰石活性影响因素研究[J].电站系统工程,2005,21(4):2-4.
[13]方婷,官民鹏.影响湿法脱硫石膏脱水效率的因素研究[J].北方环境,2011(7):186-187.
[14]丛钢,龚七一,丁宇.脱硫石膏作水泥缓凝剂研究[J].水泥,1997(3):6-8.
[15]胥桂萍,童仕唐.从FGD残渣制备α型半水石膏过程晶形的控制[J].吉林化工学院学报,2002,19(2):3-7.
[16]Singh N B,Middendorf B.Calcium sulphate hemihydrate hydration leading to gypsum crystallization[J].Progress in Crystal Growth and Characterization of Materials,2007,53(1):57-77.
[17]朱海霞.石膏基自流平砂浆的技术进展研究[J].新型建筑材料,2016(6):1-5.
[18]王舒州,陈德玉,何玉龙,等.磷石膏制备硫酸钙晶须及其应用的研究[J].新型建筑材料,2016,43(3):5-9.
[19]吴蓉.脱硫石膏-秸秆-聚苯颗粒新型墙板的试验研究[J].新型建筑材料,2016,43(7):97-99.
[20]吴敏,施惠生.矿渣及脱硫石膏-粉煤灰复合胶凝材料的试验研究[J].水泥,2008(2):1-6.