研究了温度对聚吡咯/玻璃纤维复合吸波材料的介电常数和电导率的影响。结果表明:聚吡咯/玻璃纤维复合吸波材料的介电常数实部和损耗角正切受温度影响较小。在30℃时,制备的聚吡咯/玻璃纤维复合吸波材料的介电常数虚部较大。
The effects of temperature on the dielectric constant and electrical conductivity of polypyrrole/glass fiber composite absorbing materials were studied. The results showed that the real part of the dielectric constant and the tangent of loss angle of poly-pyrrole/glass fiber composite absorbing materials were less affected by temperature. At 30 ℃,the imaginary parts of dielectric constant of prepared polypyrrole/glass fiber composite absorbing material were larger.
引文
[1]刘元军,赵家琪,赵晓明.反应温度和时间对聚苯胺/涤纶复合材料介电性能的影响[J].成都纺织高等专科学校学报,2017,34(3):13-16.
[2]刘元军,刘国熠,赵晓明.聚吡咯/聚酯纤维复合材料吸波性能的探讨[J].材料科学与工艺,2017,25(4):31-37.
[3]刘元军,刘旭琳,殷光.掺杂剂对聚苯胺/棉复合吸波材料的介电性能研究[J].纺织科学与工程学报,2018,35(3):41-46.
[4]刘元军,孙嘉瑞,张一曲,等.氧化剂种类、温度、时间对聚苯胺/棉复合吸波材料介电性能的影响[J].纺织科学与工程学报,2018,35(2):30-34.
[5]刘元军,李卫斌,赵晓明,等.聚吡咯涂层织物的介电性能研究[J].材料科学与工艺,2018,26(2):41-47.
[6]殷光,张一曲,王锡晨,等.苯胺浓度和氧化剂浓度对聚苯胺/棉复合材料的吸波性能影响[J].纺织科学与工程学报,2018,35(2):35-39.
[7]刘元军,武翔,钱学浩.氧化剂种类和浓度对聚苯胺/锦纶复合材料吸波性能的影响[J].纺织科学与工程学报,2018,35(1):56-60.
[8]刘元军,赵家琪,赵晓明.聚苯胺/涤纶复合材料的性能研究[J].染整技术,2017,39(11):17-20.
[9]武翔,刘元军,赵晓明,赵家琪.聚吡咯涂层尼龙导电织物的性能研究[J].成都纺织高等专科学校学报,2017,34(4):18-21.
[10]刘元军,刘国熠,赵晓明.滑石粉涂层复合材料的制备及其介电性能和电导率[J].材料导报,2017,31(18):28-32.
[11]刘元军,赵晓明.滑石粉涂层玻璃纤维膨体纱织物的性能研究[J].棉纺织技术,2017,45(4):27-31.
[12]赵晓明,刘元军.铁氧体/碳化硅/石墨三层涂层复合材料介电性能[J].材料工程,2017,45(1):33-37.