Characterization of the microstructures and mechanical properties of 25CrMo48V martensitic steel tempered at different times
详细信息 查看全文
- 作者：Qingfeng Wang ; Chuanyou Zhang ; Ruixin Li ; Jianzhong Gao ; Mingzhi Wang ; Fucheng Zhang
- 关键词：Martensitic steel ; Precipitation kinetics ; Johnson&ndash ; Mehl&ndash ; Avrami model ; Lath width ; Precipitate size ; Yield strength
- 刊名：Materials Science and Engineering: A
- 出版年：2013
- 出版时间：1 January, 2013
- 年：2013
- 卷：559
- 期：Complete
- 页码：130-134
- 全文大小：514 K
文摘
The microstructures of 25CrMo48V martensitic steel quenched (Q) at 900 ¡ãC and tempered (T) at 650 ¡ãC for 5-105 min were characterized by transmission electron microscope (TEM). The tensile and impact properties were evaluated from the Q-T treated samples. The results indicate that the precipitate size is increased with the prolonged soaking time and the dependence of volume fraction of precipitated particles on the tempering time follows the classical Johnson-Mehl-Avrami (JMA) model. The refinement precipitated particle could induce the enhancement of yield strength. The dependence of the yield strength of 25CrMo48V martensitic steel tempered at 650 ¡ãC for different times on the lath width and the precipitated particle size can be described as .