Mild grinding of LiNbO3/LiCoO2 and Li10GeP2S12 leaded to a well-dispersed composite electrode.
A LiNbO3/LiCoO2/Li10GeP2S12/In battery delivered a first discharge capacity of 124 mAh g− 1 when operated at 7 mA g− 1.
No significant capacity fading was observed for the LiNbO3/LiCoO2 and Li10GeP2S12 interface during electrochemical cycles.