Effect of prior cyclic oxidation on the creep behavior of directionally solidified (DS) CM-247LC alloy

详细信息    查看全文

• 作者：Md Zafir Alam ; ^{zafir@dmrl.drdo.in} ; D.V.V. Satyanarayana ; D. Chatterjee ; R. Sarkar ; D.K. Das
• 关键词：Creep ; Superalloy ; Oxidation ; Recrystallization ; Precipitate-free zone
• 刊名：Materials Science and Engineering: A
• 出版年：2012
• 出版时间：28 February 2012
• 年：2012
• 卷：536
• 期：Complete
• 页码：14-23
• 全文大小：2904 K

文摘

The effect of cyclic oxidation exposure on the tensile creep properties of a directionally solidified Ni-base superalloy (CM-247LC) has been evaluated at a stress-temperature combination of 220 MPa/980 ¡ãC. Cyclic oxidation of creep specimens has been carried out 1100 ¡ãC in air up to 750 h. The creep properties (creep rate, creep strain and creep life) were found to be adversely affected by the oxidation exposure. The extent of degradation of the properties increased with increase in the duration of oxidation. Such deterioration of creep properties of the alloy has been correlated with the surface damage and general microstructural degradation that occur in the alloy during oxidation exposure.