The superamphiphobic EP/MPVDF/FEP composite coating could reach up to a contact angle of 166° and 155° to water and glycerol, respectively.
The wear life of the EP composite coating with 25 wt.% FEP was improved to 18 times longer than the pure EP coating.
The intrinsic brittleness of EP was successfully avoided by introducing the malleable MPVDF.
The electrochemical corrosion current of the prepared composite coating gradually decreased from 10−3.5 to 10−5.5 mA/cm2 with further increase of FEP loading.