Correlating Titania Nanostructured Morphologies with Performance as Anode Materials for Lithium-Ion Batteries

详细信息    查看全文

• 作者：Crystal S. Lewis ; Yue Ru Li ; Lei Wang ; Jing Li ; Eric A. Stach ; Kenneth J. Takeuchi ; Amy C. Marschilok ; Esther S. Takeuchi ; Stanislaus S. Wong
• 刊名：ACS Sustainable Chemistry & Engineering
• 出版年：2016
• 出版时间：December 5, 2016
• 年：2016
• 卷：4
• 期：12
• 页码：6299-6312
• 全文大小：808K
• ISSN：2168-0485

文摘

Titanium oxide is a ubiquitous and commonly used material in the environment. Herein, we have systematically probed the use of various hydrothermally derived titania (TiO₂) architectures including zero-dimensional (0D) nanoparticles, one-dimensional (1D) nanowires, and three-dimensional (3D) urchin-like motifs as anode materials for lithium-ion batteries. The structure and morphology of these nanomaterials were characterized using electron microscopy. The surface areas of these materials were quantitatively analyzed through Brunauer–Emmett–Teller (BET) adsorption measurements and were found to be relatively similar for both 1D and 3D samples with a slightly higher surface area associated with the 0D nanoparticles. Hence, to normalize for the surface area effect, readily available 0D commercial nanoparticles (Degussa P25), which possessed a similar surface area to that of as-prepared 1D and 3D materials, were also analyzed. Electrochemical analysis revealed a superior performance of hydrothermally derived 3D urchin-like motifs as compared with both as-prepared 0D and 1D samples as well as commercial Degussa P25. Our studies suggest the greater overall importance of morphology as opposed to surface area in dictating the efficiency of the Li ion diffusion process. Specifically, the 3D urchins yielded consistent rate capabilities, delivering 214, 167, 120, 99, and 52 mAh/g under corresponding discharge rates of 0.1, 1, 10, 20, and 50 C, respectively. Moreover, these 3D motifs gave rise to a stable cycling performance, exhibiting a capacity retention of ∼90% in cycles 1–100 under a discharge rate of 1 C. Furthermore, the rate capability and cycling performance of our 3D hierarchical motifs were (i) comparable to those of anatase TiO₂/TiO₂-(B) hybrid structures even with little if any electrochemically promising bronze (B) phase herein and (ii) clearly enhanced as compared with previous results using similar anatase 3D microspheres.