High-Pressure Water Intrusion Investigation of Pure Silica ITQ-7 Zeolite

详细信息    查看全文

• 作者：Lydie Tzanis ; Bernd Marler ; Hermann Gies ; Jo毛l Patarin
• 刊名：The Journal of Physical Chemistry C
• 出版年：2013
• 出版时间：February 28, 2013
• 年：2013
• 卷：117
• 期：8
• 页码：4098-4103
• 全文大小：319K
• 年卷期：v.117,no.8(February 28, 2013)
• ISSN：1932-7455

文摘

Experimental water intrusion鈥揺xtrusion isotherms were recorded at room temperature on pure silica ISV-type zeolite (ITQ-7 zeosil) possessing a 3D channel system. The water intrusion is obtained by applying a high hydraulic pressure corresponding to the intrusion step. When the pressure is released, the water extrusion occurs but at a lower pressure to that of the intrusion one. The ITQ-7 zeosil鈥搘ater system behaves like a shock-absorber, but the phenomenon is nonreproducible. Several characterizations have been realized before and after water intrusion鈥揺xtrusion experiments in order to reveal the presence or the absence of defects after such experiments. Structural modifications at the long-range order can be observed by XRD analysis after intrusion. At the short-range order, solid-state NMR spectroscopy shows evidence of the presence of Q₂ ((HO鈭?₂Si(鈭扥Si)₂) and Q₃ ((HO鈥揝i(鈭扥Si)₃) or (Si(鈭扥Si)₃O^{鈥?/sup>)) groups revealing the breaking of some siloxane bridges after the intrusion step. The amount of defects increases (<2% before and 15% after intrusion step). However, after a regeneration step (calcination of the intruded-extruded sample), the ITQ-7 zeosil鈥搘ater system displays again a shock-absorber behavior with a similar intrusion pressure.}