Correspondence between susceptibility to SCC of 7050 aluminum alloy and passive film-induced stress at various pH values
详细信息 查看全文
- 作者：Xing Qi 祁星 ; Renguo Song 宋仁国 ; Wenjuan Qi…
- 关键词：Key words7050 aluminum alloy ; susceptibility to SCC ; pH value ; passive film ; induced stress
- 刊名：Journal of Wuhan University of Technology-Mater. Sci. Ed.
- 出版年：2017
- 出版时间：February 2017
- 年：2017
- 卷：32
- 期：1
- 页码：173-178
- 全文大小：
- 刊物类别：Chemistry and Materials Science
- 刊物主题：Materials Science, general;
- 出版者：Wuhan University of Technology
- ISSN：1993-0437
- 卷排序：32
文摘
The passive film-induced stress and the susceptibility to SCC of 7050 aluminum alloy in 3.5% sodium chloride solution at various pH values were investigated by slow strain rate testing (SSRT) and flowing stress differential method. The results showed that the passive film-induced stress and the susceptibility to SCC decreased with increasing pH values when pH≤7, while they increased with increasing pH values when pH >7. However, the corrosion type was interpreted as exfoliation corrosion when pH=1 and 14, and there was no film formed on the surface of the specimens. The whole variation plots of film-induced stress and the SCC susceptibility with pH values were both presented as a valley shape. The symbol and amount of the film-induced stress were related to the compositions of the passive film, which were analyzed using X-ray photoelectron spectroscopy (XPS).