摘要
A new bimetallic catalyst (Ag–Co/CeO2) was studied for simultaneously catalytic removal of NO and CO in the absence or presence of O2. CeO2 prepared by homogeneous precipitation method was optimized as supports for the active components. The addition of Ag on CeO2 greatly improved the catalytic activities in the lower temperature regions (300 °C), and the introduction of Co on CeO2 increased the activities at higher temperatures (250 °C). The bimetallic Ag–Co/CeO2 catalyst combined the advantages of the corresponding individual metal supported catalysts and showed superior activity due to the synergetic effect. The effect of support, temperature, loading amount, GHSV and oxygen on catalysis was investigated. NO and CO could be completely removed in the temperature range of 200–600 °C at a very high space velocity of 120 000 h−1. No deactivation was observed over 4%Ag–0.4%Co/CeO2 catalyst even after 50 h test.