Microstructural evolution and tensile properties of the in situ Al-15%Mg₂Si composite with extra Si contents

详细信息	查看全文 | 推荐本文 |

• 作者：N. Nasiri ; M. Emamy ; ^{emamy@ut.ac.ir} ; A. Malekan
• 关键词：A. Metal matrix composite ; C. Casting ; G. Fractography
• 刊名：Materials and Design
• 出版年：2012
• 期刊代码：56_02613069
• 类别：ms
• 出版时间：May, 2012
• 卷：37
• 期：Complete
• 页码：215-222
• 文件大小：2425 K

摘要

In the present work, the effect of extra Si addition on the microstructure and tensile properties of Al-15%Mg₂Si composite has been investigated. The Al-15%Mg₂Si composite ingot was made by in situ process and different amounts of extra Si (0.5, 1, 1.5, 2, 5 and 7 wt.%Si) were added to the remelted composite. Optical microscopy and scanning electron microscopy (SEM) indicated that the addition of extra Si up to 2 wt.%, reduces the average Mg₂Si particle size from 39 渭m to 26 渭m and increases the volume fraction of 伪-Al phase from 6%to 22%. Addition of extra Si content up to 7 wt.%leads to the formation of primary Mg₂Si particles with larger size (38 渭m). The results of tensile test revealed that the addition of extra Si improves ultimate tensile strength (UTS) and elongation values of the composite from 176 MPa and 1.7%to 222 MPa and 3.0%respectively. Fractographic analysis of specimens exposed a cellular nature for the fracture surface. On the cellular fracture surface, the features of both brittle and ductile fracture were present simultaneously. Raising the amount of extra Si up to 7%has increased the number and decreased the size of dimples. These microstructural findings led to a change in the mode of fracture from brittle to ductile and increased elongation values.