CIGS thin-film solar cells and modules on enamelled steel substrates

详细信息	查看全文 | 推荐本文 |

• 作者：R. Wuerz^a ; ^{roland.wuerz@zsw-bw.de} ; A. Eicke^a ; F. Kessler^a ; S. Paetel^a ; S. Efimenko^b ; C. Schlegel^b
• 关键词：Cu(In ; Ga)Se2 ; Low-carbon steel ; Enamel ; Na ; K ; Doping
• 刊名：Solar Energy Materials and Solar Cells
• 出版年：2012
• 期刊代码：81_09270248
• 类别：ce
• 出版时间：May, 2012
• 卷：100
• 期：Complete
• 页码：132-137
• 文件大小：619 K

摘要

The charm of Cu(In_1鈭?em>xGa_x)Se₂ (CIGS) thin-film solar cells is their potential for flexible, low-weight modules. Steel foil is an attractive candidate for use as a flexible substrate material as it is stable at the high temperatures involved during CIGS processing and is also commercially available. For monolithic series connection of the single cells to a module, an insulating layer is needed on the conducting steel substrate. We tested enamel layers on low-carbon steel as the insulating layer, as source a of sodium doping, and also as a diffusion barrier layer to suppress the diffusion of detrimental elements from the substrate into the CIGS layer, which is more pronounced on mild steel compared to stainless steel. Using enamelled steel, we could achieve a maximum cell efficiency of 17.6%(certified) and a module efficiency of 15.0%on a 10脳10 cm² substrate (aperture area=48 cm虏) with a high temperature multi-stage inline CIGS process. The open-circuit voltage and short-circuit current density values of cells and modules prepared in the multi-stage CIGS process used here were often higher on enamelled steel than on the standard soda lime glass substrates.