摘要
Synthetic porous calcium hydroxyapatite (noted p-HAp) treated with different fluoride concentrations at room temperature in the presence of carbonate, sodium chloride and phosphate-rich media was investigated. The fluoridation rate of the porous calcium hydroxyapatite was 89%using 1mol/L [F−] solution compared with 30%for crystalline hydroxyapatite (c-HAp). The high specific surface area of p-HAp (235m2g−1) compared with c-HAp sample (47m2g−1) has an important effect on the removal of fluoride ions from aqueous solution, when p-HAp was treated with high fluoride concentration to produce calcium fluorohydroxyapatite materials. Fluoride adsorption on porous hydroxyapatites (p-HAp) modified their structural and conduction properties.