In this respect, the present investigation deals with the application of a continuous wave high power diode laser to post-treat Diamalloy 2002 deposited by HVOF on AA 6082 T6 aluminum alloy. Different laser power and scan speed were investigated in order to identify the process window most favorable to improve the overall mechanical property of Diamalloy 2002 coatings. The changes in morphology, micro-structure and chemical composition of the coatings after laser post-treatments were investigated by inductive gage profilometry and combined SEM-EDXS. Further, the changes in the mechanical properties of the coatings were investigated in terms of hardness, elastic modulus, scratch and wear resistance. Consistent improvements in mechanical property can be achieved by Diamalloy 2002 when laser processing is performed at higher power and reduced scan speed. Yet, too much increase in power density should be always avoided as it can be detrimental to the final property of the coatings and cause high defectiveness and their failure.