Effect of simultaneous ion irradiation on microstructural change of SiC/SiC composites at high temperature

详细信息	查看全文 | 推荐本文 |

• 作者：Taguchi ; T. ; Wakai ; E. ; Igawa ; N. ; Nogami ; S. ; Snead ; L.L. ; Hasegawa ; A. ; Jitsukawa ; S.
• 关键词：E0300 ; I0400 ; M0500 ; S0400
• 刊名：Journal of Nuclear Materials
• 出版年：2002
• 期刊代码：51_00223115
• 类别：ms
• 出版时间：December, 2002
• 卷：307-311
• 期：Part 2
• 页码：1135-1140
• 文件大小：205 K

摘要

The effect of simultaneous triple ion irradiation of He, H and Si on microstructural evolution of two kinds of SiC/SiC composites (HNS composite (using Hi-Nicalon type S SiC fiber) and TSA composite (using Tyranno SA SiC fiber)) at 1000 °C has been investigated. The microstructure observations of SiC/SiC composites irradiated to 10 dpa were examined by transmission electron microscopy. He bubbles were hardly formed in matrix of TSA composite, but many helium bubbles and some cracks were observed at grain boundaries of matrix of HNS composite. He bubbles and cracks were not, on the other hand, observed in the both fiber fabrics of HNS and TSA composites. Debonding between fiber and carbon layer following irradiation region was not observed in the both composites. Under these irradiation conditions, TSA composite showed the better microstructural stability against ion beams irradiation than one of HNS composite.