摘要
对Cr-Al铁素体不锈钢在退火过程中的微观织构演变进行了研究。运用EBSD技术表征了随退火时间的延长,再结晶行为和微观织构的演变规律,并用HKL Channel系统进行了量化分析;测试了塑性应变比r的变化规律。结果表明,大部分的再结晶行为发生在保温过程的前10min。当保温时间由2min延长至10min后,完全再结晶晶粒所占的比例由3.5%提高到89%,而在后续的保温过程中变化不大;退火时间短于10min时,以{hkl}<110>织构为主,大于10min后,{111}织构比例快速增加;退火时间为30min时,r值达到最大值,约为1.27,具有最优的成形性能。
The texture evolution of Cr-Al ferritic stainless steel during annealing treatment was observed.The recrystallization behavior and texture evolution were characterized by EBSD technique and analyzed quantitatively using HKL Channel.The plastic-strain ratio r value was tested.The results indicate that most of the recrystallization process occurs with annealing time less than 10 min.The recrystallization fraction is increased from 3.5%to89% with annealing time from 2min to 10 min.When further holding treatment,the recrystallization behavior keeps stable.The texture is mainly{hkl}<110>type when annealing time is less than 10 min,and it is{111}type with annealing time more than 10 min.The r vale reaches the peak value of 1.27 when annealing time is 30 min,exhibiting the desirable formability.
引文
[1] OGWU A A,DAVIES T J.Improving the sensitization resistance of ferritic stainless steels[J].Scripta Materialia,1997,37(3):259-263.
[2] HUGH M Y,ENGLER O.Effect of intermediate annealing on texture,formability and ridging of 17%Cr ferritic stainless steel sheet[J].Materials Science and Engineering,2001,A308(1-2):74-87.
[3]杨平,常守海,孙祖庆.低碳钢铁素体热变形过程中的取向成像分析[J].材料研究学报,2003,17(5):520-529.
[4]杨玉芳,杨正山,王珺,等.冷轧变形率对超纯铁素体不锈钢439板材退火组织与性能的影响[J].材料热处理学报,2018,39(8):68-74.
[5] SHIN H J,AN J K.The effect of texture on ridging of ferritic stainless steel[J].Acta Materialia,2003(51):4 693-4 706.
[6] WEI L L,ZHENG J H,CHEN L Q,et al.High temperature oxidation behavior of ferritic stainless steel containing W and Ce[J].Corrosion Science,2018,142:79-92.
[7] CAI G J,LI C S,WANG D G,et al.Investigation of annealing temperature on microstructure and texture of Fe-19Cr-2Mo-Nb-Ti ferritic stainless steel[J].Materials Characterization,2018,141:169-176.
[8]向红亮,刘春育,王永霞,等.含Cu抗菌双相不锈钢的空蚀行为研究[J].特种铸造及有色合金,2018,38(8):816-820.
[9] ADHIKARY M,CHAKRABORTY A,DAS A,et al.Influence of annealing texture on dynamic tensile deformation characteristics of dual phase steel[J].Materials Science and Engineering,2018,A736:209-218.