含金耐磨耐蚀涂层的制备及性能研究进展
|
摘要
材料在使用过程中经常会因为磨损和腐蚀而导致失效,采用表面改性技术制备涂层来改善材料的耐磨性和耐蚀性是一种经济、高效的方法。由于金具有低剪切强度、化学稳定性好和自润滑作用等优点,在涂层中引入金可以显著改善材料的耐磨性和耐蚀性。综述了含金耐磨耐蚀涂层目前主要的制备方法、金的润滑机理、金提高涂层耐蚀性的原因及其影响因素等,并对涂层的发展方向进行了展望。
Materials gradually fail due to abrasion and corrosion during use. It is an economical and efficient method to prepare coating by surface modification techniques to improve the abrasion resistance and corrosion resistance of materials. Due to the low shear strength, good chemical stability and self-lubricating of Au, the introduction of Au into the coatings can significantly improve the abrasion resistance and corrosion resistance of materials. The main preparation methods, the lubrication mechanisms and the reasons for improving the corrosion resistance of Au were reviewed, and the development direction of coatings were also summarized.
Materials gradually fail due to abrasion and corrosion during use. It is an economical and efficient method to prepare coating by surface modification techniques to improve the abrasion resistance and corrosion resistance of materials. Due to the low shear strength, good chemical stability and self-lubricating of Au, the introduction of Au into the coatings can significantly improve the abrasion resistance and corrosion resistance of materials. The main preparation methods, the lubrication mechanisms and the reasons for improving the corrosion resistance of Au were reviewed, and the development direction of coatings were also summarized.
引文
[1]慕伟意,李争显,杜继红,等.镁合金的应用及其表面处理研究进展[J].表面技术,2011,40(2):86-91.MU W Y,LI Z X,DU J H,et al.Application and surface treatment research progress of magnesium alloys[J].Surface technology,2011,40(2):86-91.
[2]王孟君,黄电源,姜海涛.汽车用铝合金的研究进展[J].金属热处理,2006,31(9):34-38.WANG M J,HUANG D Y,JIANG H T.Research progress of aluminium alloys for the automotive industry[J].Heat treatment of metals,2006,31(9):34-38.
[3]张晓燕,张家鼎,吴正纯,等.新型复合电接触材料的开发研究[J].上海大学学报(自然科学版),2000,6(1):91-94.ZHANG X Y,ZHANG J D,WU Z C,et al.The research and development on a new type composite electrocontact material[J].Journal of Shanghai University(Natural science edition),2000,6(01):91-94.
[4]孙振宇.表面强化技术在机械零件中的应用[J].煤矿机械,2008,29(10):85-86.SUN Z Y.Application of surface strengthening technology in mechanical parts[J].Coal mine machinery,2008,29(10):85-86.
[5]张立德.纳米材料和纳米结构[J].中国科学院院刊,2001,16(6):444-445.ZHANG L D.Nanomaterials and nanostructures[J].Bulletin of Chinese Academy of Sciences,2001,16(6):444-445.
[6]FUJITA T,GUAN P,MCKENNA K,et al.Atomic origins of the high catalytic activity of nanoporous gold[J].Nature materials,2012,11(9):775.
[7]KINBARA A,BABA S.Selected mechanical properties of gold,silver,aluminium and germanium coatings[J].Thin solid films,1980,72(2):211-221.
[8]徐滨士,欧忠文,马世宁,等.纳米表面工程[J].中国机械工程,2000,11(6):707-712.XU B S,OU Z W,MA S N,et al.Nano-surfaceengineering[J].China mechanical engineering,2000,11(6):707-712.
[9]胡虹,吴波.镍钨合金中间层对铜基体镀薄金体系耐蚀性的影响[J].电镀与涂饰,2016,35(24):1277-1280.HU H,WU B.Effect of nickel-tungsten alloy intermediate coating on corrosion resistance of thin gold coating system on copper substrate[J].Electroplating&Finishing,2016,35(24):1277-1280.
[10]刘韧,李海燕,李佳.提高石英基片Cr/Au掩膜抗腐蚀性的试验性研究[C].北京:惯性技术发展动态发展方向研讨会,2011.LIU R,LI H Y,LI J.Experimental study on improving corrosion resistance of Cr/Au mask film on quartz wafer[C].Beijing:A seminar on the trend of development of inertial technology,2011.
[11]ZHANG K,SHARMA S.Site-selective,low-loading,Au nanoparticle-polyaniline hybrid coatings with enhanced corrosion resistance and conductivity for fuel cells[J].ACS sustainable chemistry&engineering,2017,5(1):277-286.
[12]顾培夫.薄膜技术[M].杭州:浙江大学出版社,1990.GU P F.Thin film technique[M].Hangzhou:Zhejiang University Press,1990.
[13]马景灵,任风章,孙浩亮.磁控溅射镀膜技术的发展及应用[J].中国科教创新导刊,2013(29):136.MA J L,REN F Z,SUN H L.Development and application of magnetron sputtering coating technology[J].China education innovation herald,2013(29):136.
[14]刘艳松,何智兵,李俊,等.磁控溅射制备成分渐变Au/Cu复合涂层的研究[J].原子能科学技术,2014,48(5):955-960.LIU Y S,HE Z B,LI J,et al.Fabrication of Au/Cu graded bimetallic alloy coating with DC magnetron sputtering[J].Atomic energy science and technology,2014,48(5):955-960.
[15]SIMMONDS M C,SWYGENHOVEN H V,PFLüGER E,et al.Magnetron sputter deposition and characterisation of Ti/TiN,Au/TiN and MoSx/Pb multilayers[J].Surface&coatings technology,1997(s94/95):490-494.
[16]郭珊云,周光月,陈志全,等.铂族金属化学气相沉积[J].贵金属,2000,21(4):49-53.GUO S Y,ZHOU G Y,CHEN Z Q,et al.Platinum metals chemical vapor deposition[J].Precious metals,2000,21(4):49-53.
[17]胡昌义,李靖华.化学气相沉积技术与材料制备[J].稀有金属,2001,25(5):364-368.HU C Y,LI J H.Chemical vapor deposition and preparation of materials[J].Chinese journal of rare metals,2001,25(5):364-368.
[18]FEURER E,SUHR H.Preparation of gold films by plasma-CVD[J].Applied physics A,1987,44(2):171-175.
[19]SHEDD G M,LEZEC H,DUBNER A D,et al.Focused ion beam induced deposition of gold[J].Applied physics letters,1986,49(23):1584-1586.
[20]KOOPS H,KRETZ J,RUDOLPH M,et al.Characterization and application of materials grown by electron-beam-induced deposition[J].Japanese journal of applied physics,1994,33(Part 1,No.12B):7099-7107.
[21]BOTMAN A,MULDERS J J L,WEEMAES R,et al.Purification of platinum and gold structures after electron-beam-induced deposition[J].Nanotechnology,2006,17(15):3779-3785.
[22]曾伟,周海晖,英晓芳,等.电极/反相微乳液体系电沉积制备纳米金镀层[J].物理化学学报,2007,23(5):769-773.ZENG W,ZHOU H H,YING X F,et al.Electrodeposition of gold nanoparticles coatings from electrode/reverse microemulsion system[J].Acta physicochimica sinica,2007,23(5):769-773.
[23]朱冬生,赵朝晖,吴会军,等.溶胶-凝胶法制备纳米薄膜的研究进展[J].材料导报,2003,17(f09):53-55.ZHU D S,ZHAO Z H,WU H J,et al.Advances in synthesis of nano-thin films by sol-gel method[J].Materials review,2003,17(f09):53-55.
[24]HU Y,SHI Q,HUANG W,et al.Preparation and phase transition properties of Ti-doped VO2 films by sol-gel process[J].Journal of sol-gel science and technology,2015,78(1):1-7.
[25]邱训高,郭鹤桐,周玉福.电沉积Au-MoS2复合减摩镀层[J].天津大学学报(自然科学与工程技术版),1988(3):30-35.QIU X G,GUO H T,ZHOU Y F.Electrodeposition of Au-MoS2 composite antifriction coating[J].Journal of Tianjin University(Science and technology),1988(3):30-35.
[26]REZRAZI M,DOCHE M L,BER?OT P,et al.Au-PTFEcomposite coatings elaborated under ultrasonic stirring[J].Surface&coatings technology,2005,192(1):124-130.
[27]陈云霞,刘维民,张平余,等.纳米Au-TiO2复合薄膜的溶胶-凝胶法制备、表征和性能[J].高等学校化学学报,2002,23(8):1574-1578.CHEN Y X,LIU W M,ZHANG P Y,et al.Preparation,characterization and properties of nano Au-TiO2composite thin films by sol-gel process[J].Chemical journal of Chinese universities,2002,23(8):1574-1578.
[28]张丽仙,赵铱民,邵龙泉,等.牙用镍铬合金表面不同涂层电化学腐蚀研究[J].实用口腔医学杂志,2009,25(4):471-474.ZHANG L X,ZHAO Y M,SHAO L Q,et al.A research on the corrosion resistance of Ni-Cr alloy with different coatings[J].Journal of practical stomatology,2009,25(4):471-474.
[29]刘维民,薛群基,周静芳,等.纳米颗粒的抗磨作用及作为磨损修复添加剂的应用研究[J].中国表面工程,2001,14(3):21-23.LIU W M,XUE Q J,ZHOU J F,et al.The anti wear function of nanoparticles and their application in abrasion repairing additive[J].China surface engineering,2001,14(3):21-23.
[30]张蕊,王鲁宁,赵飞,等.贵金属在船用钛及钛合金表面改性中的应用[J].贵金属,2017,38(4):74-80.ZHANG R,WANG L N,ZHAO F,et al.Application and development trend of precious metals in the surface modification of marine titanium and titanium alloys[J].Precious metals,2017,38(4):74-80.
[31]BAHADUR S,SUNKARA C.Effect of transfer film structure,composition and bonding on the tribological behavior of polyphenylene sulfide filled with nano particles of TiO2,ZnO,CuO and SiC[J].Wear,2005,258(9):1411-1421.
[32]OKINAKA Y.Significance of inclusions in electroplated gold films for electronics applications[J].Gold bulletin,2000,33(4):117-127.
[33]杨长江,陈国需,赵立涛,等.纳米软金属作为自修复润滑添加剂的研究进展[J].润滑与密封,2009,34(5):115-117.YANG C J,CHEN G X,ZHAO L T,et al.Research progress of soft metal nanoparticles as self-repairing lubricant additive[J].Lubrication and sealing,2009,34(5):115-117.
[34]方芬,颜红侠,张军平.纳米粒子在润滑材料中的应用进展[J].材料保护,2006,39(12):32-36.FANG F,YAN H X,ZHANG J P.Application progress of nanoparticles in lubricating materials[J].Material protection,2006,39(12):32-36.
[35]于立岩,郝春成,隋丽娜,等.纳米粒子改善润滑油摩擦磨损性能的研究[J].材料科学与工程学报,2004,22(6):901-905.YU L Y,HAO C C,SUI L N,et al.Study on the improving friction and wear properties of lubricating oil with nanoparticles[J].Journal of materials science and engineering,2004,22(6):901-905.
[36]于德洋,翁立军,欧阳锦林.空间机械润滑研究的发展现状[J].摩擦学学报,1996,16(1):89-96.YU D Y,WENG L J,OUYANG J L.Current development situation of space mechanical lubrication[J].Journal of tribology,1996,16(1):89-96.
[37]ROBERTS E W,WILLIAMS B J,OGILVY J A.The effect of substrate surface roughness on the friction and wear of sputtered MoS2 films[J].Journal of physics DApplied physics,1992,25(1A):A65.
[38]KONG L,ZHU S,QIAO Z,et al.Effect of Mo and Ag on the friction and wear behavior of ZrO2,(Y2O3)-AgCaF2-Mo composites from 20°C to 1000°C[J].Tribology international,2014,78(78):7-13.
[39]STOYANOV P,GUPTA S,CHROMIK R R,et al.Microtribological performance of Au-MoS2 nanocomposite and Au/MoS2 bilayer coatings[J].Tribology international,2012,52(3):144-152.
[40]DAI L Y,MENG R G,CHEN J F,et al.Research progress on nanoparticles for metal wear self-repairing[J].China ship repair,2012,25(04):33-36.
[41]郑林庆.摩擦学原理[M].北京:高等教育出版社,1994.ZHENG L Q.Principles of tribology[M].Beijing:Higher Education Press,1994.
[42]王新平,肖金坤,张雷,等.载荷对AuNi9/金镀层摩擦副摩擦磨损性能的影响[J].中国有色金属学报,2012,22(12):3427-3431.WANG X P,XIAO J K,ZHANG L,et al.Effect of load on friction and wear behavior of AuNi9/Au coating tribocouple[J].The Chinese journal of nonferrous metals,2012,22(12):3427-3431.
[43]STOYANOV P,CHROMIK R R,GOLDBAUM D,et al.Microtribological performance of Au-MoS2,and Ti-MoS2,coatings with varying contact pressure[J].Tribology letters,2010,40(1):199-211.
[44]LI J,ZHANG H,FAN A,et al.Tribological properties characterization of Ti/Cu/N thin films prepared by DCmagnetron sputtering on titanium alloy[J].Surface and coatings technology,2016,294:30-35.
[45]ANTLER M,DROZDOWICZ M H.Fretting corrosion of gold-plated connector contacts[J].Wear,1981,74(1):27-50.
[46]WANG Y,YING J,WEI S,et al.Au-Ni-TiO2 nanocomposite coatings prepared by sol-enhanced method[J].Journal of the electrochemical society,2014,161(14):775-781.
[47]王其明,徐锦芬,党鸿辛.MoS2-Au共溅膜的结构与性能之研究[J].摩擦学学报,1990,10(2):84-95.WANG Q M,XU J F,DANG X H.A study on the structures and performances of MoS2-Au co-sputtered films[J].Tribology,1990,10(2):84-95
[48]LIN S S,HUANG J L,?AJGALIK P.The properties of heavily Al-doped ZnO films before and after annealing in the different atmosphere[J].Thin solid films,2004,185(2/3):254-263.
[49]TORRELL M,CUNHA L,CAVALEIRO A,et al.Functional and optical properties of Au:TiO2,nanocomposite films:The influence of thermal annealing[J].Applied surface science,2010,256(22):6536-6542.
[50]HVOLB?K B,JANSSENS T V W,CLAUSEN B S,et al.Catalytic activity of Au nanoparticles[J].Nano today,2007,2(4):14-18.
[51]LI G,WANG Y,CAO Z.Effect of refined grain size on corrosion behavior of metal Cr in media containing chloride ions[J].Ciesc journal,2012,63(2):560-566.
[52]SHORES D A.Corrosion and metal release rates of Ni substrates under a porous gold coating[J].Corrosion science,2008,50(2):372-383.
[53]BUELENS C,CELIS J P,ROOS J R.Electrochemical aspects of the plating of gold and composite gold-alumina[J].Transactions of the IMF,1985,63(1):6-10.
[54]GUZMáN P,APERADOR W,YATE L.Enhancement of the pitting corrosion resistance of AISI 316LVM steel with Ta-Hf-C/Au bilayers for biomedical applications[J].Journal of nanomaterials,2017(1):1-10.
[2]王孟君,黄电源,姜海涛.汽车用铝合金的研究进展[J].金属热处理,2006,31(9):34-38.WANG M J,HUANG D Y,JIANG H T.Research progress of aluminium alloys for the automotive industry[J].Heat treatment of metals,2006,31(9):34-38.
[3]张晓燕,张家鼎,吴正纯,等.新型复合电接触材料的开发研究[J].上海大学学报(自然科学版),2000,6(1):91-94.ZHANG X Y,ZHANG J D,WU Z C,et al.The research and development on a new type composite electrocontact material[J].Journal of Shanghai University(Natural science edition),2000,6(01):91-94.
[4]孙振宇.表面强化技术在机械零件中的应用[J].煤矿机械,2008,29(10):85-86.SUN Z Y.Application of surface strengthening technology in mechanical parts[J].Coal mine machinery,2008,29(10):85-86.
[5]张立德.纳米材料和纳米结构[J].中国科学院院刊,2001,16(6):444-445.ZHANG L D.Nanomaterials and nanostructures[J].Bulletin of Chinese Academy of Sciences,2001,16(6):444-445.
[6]FUJITA T,GUAN P,MCKENNA K,et al.Atomic origins of the high catalytic activity of nanoporous gold[J].Nature materials,2012,11(9):775.
[7]KINBARA A,BABA S.Selected mechanical properties of gold,silver,aluminium and germanium coatings[J].Thin solid films,1980,72(2):211-221.
[8]徐滨士,欧忠文,马世宁,等.纳米表面工程[J].中国机械工程,2000,11(6):707-712.XU B S,OU Z W,MA S N,et al.Nano-surfaceengineering[J].China mechanical engineering,2000,11(6):707-712.
[9]胡虹,吴波.镍钨合金中间层对铜基体镀薄金体系耐蚀性的影响[J].电镀与涂饰,2016,35(24):1277-1280.HU H,WU B.Effect of nickel-tungsten alloy intermediate coating on corrosion resistance of thin gold coating system on copper substrate[J].Electroplating&Finishing,2016,35(24):1277-1280.
[10]刘韧,李海燕,李佳.提高石英基片Cr/Au掩膜抗腐蚀性的试验性研究[C].北京:惯性技术发展动态发展方向研讨会,2011.LIU R,LI H Y,LI J.Experimental study on improving corrosion resistance of Cr/Au mask film on quartz wafer[C].Beijing:A seminar on the trend of development of inertial technology,2011.
[11]ZHANG K,SHARMA S.Site-selective,low-loading,Au nanoparticle-polyaniline hybrid coatings with enhanced corrosion resistance and conductivity for fuel cells[J].ACS sustainable chemistry&engineering,2017,5(1):277-286.
[12]顾培夫.薄膜技术[M].杭州:浙江大学出版社,1990.GU P F.Thin film technique[M].Hangzhou:Zhejiang University Press,1990.
[13]马景灵,任风章,孙浩亮.磁控溅射镀膜技术的发展及应用[J].中国科教创新导刊,2013(29):136.MA J L,REN F Z,SUN H L.Development and application of magnetron sputtering coating technology[J].China education innovation herald,2013(29):136.
[14]刘艳松,何智兵,李俊,等.磁控溅射制备成分渐变Au/Cu复合涂层的研究[J].原子能科学技术,2014,48(5):955-960.LIU Y S,HE Z B,LI J,et al.Fabrication of Au/Cu graded bimetallic alloy coating with DC magnetron sputtering[J].Atomic energy science and technology,2014,48(5):955-960.
[15]SIMMONDS M C,SWYGENHOVEN H V,PFLüGER E,et al.Magnetron sputter deposition and characterisation of Ti/TiN,Au/TiN and MoSx/Pb multilayers[J].Surface&coatings technology,1997(s94/95):490-494.
[16]郭珊云,周光月,陈志全,等.铂族金属化学气相沉积[J].贵金属,2000,21(4):49-53.GUO S Y,ZHOU G Y,CHEN Z Q,et al.Platinum metals chemical vapor deposition[J].Precious metals,2000,21(4):49-53.
[17]胡昌义,李靖华.化学气相沉积技术与材料制备[J].稀有金属,2001,25(5):364-368.HU C Y,LI J H.Chemical vapor deposition and preparation of materials[J].Chinese journal of rare metals,2001,25(5):364-368.
[18]FEURER E,SUHR H.Preparation of gold films by plasma-CVD[J].Applied physics A,1987,44(2):171-175.
[19]SHEDD G M,LEZEC H,DUBNER A D,et al.Focused ion beam induced deposition of gold[J].Applied physics letters,1986,49(23):1584-1586.
[20]KOOPS H,KRETZ J,RUDOLPH M,et al.Characterization and application of materials grown by electron-beam-induced deposition[J].Japanese journal of applied physics,1994,33(Part 1,No.12B):7099-7107.
[21]BOTMAN A,MULDERS J J L,WEEMAES R,et al.Purification of platinum and gold structures after electron-beam-induced deposition[J].Nanotechnology,2006,17(15):3779-3785.
[22]曾伟,周海晖,英晓芳,等.电极/反相微乳液体系电沉积制备纳米金镀层[J].物理化学学报,2007,23(5):769-773.ZENG W,ZHOU H H,YING X F,et al.Electrodeposition of gold nanoparticles coatings from electrode/reverse microemulsion system[J].Acta physicochimica sinica,2007,23(5):769-773.
[23]朱冬生,赵朝晖,吴会军,等.溶胶-凝胶法制备纳米薄膜的研究进展[J].材料导报,2003,17(f09):53-55.ZHU D S,ZHAO Z H,WU H J,et al.Advances in synthesis of nano-thin films by sol-gel method[J].Materials review,2003,17(f09):53-55.
[24]HU Y,SHI Q,HUANG W,et al.Preparation and phase transition properties of Ti-doped VO2 films by sol-gel process[J].Journal of sol-gel science and technology,2015,78(1):1-7.
[25]邱训高,郭鹤桐,周玉福.电沉积Au-MoS2复合减摩镀层[J].天津大学学报(自然科学与工程技术版),1988(3):30-35.QIU X G,GUO H T,ZHOU Y F.Electrodeposition of Au-MoS2 composite antifriction coating[J].Journal of Tianjin University(Science and technology),1988(3):30-35.
[26]REZRAZI M,DOCHE M L,BER?OT P,et al.Au-PTFEcomposite coatings elaborated under ultrasonic stirring[J].Surface&coatings technology,2005,192(1):124-130.
[27]陈云霞,刘维民,张平余,等.纳米Au-TiO2复合薄膜的溶胶-凝胶法制备、表征和性能[J].高等学校化学学报,2002,23(8):1574-1578.CHEN Y X,LIU W M,ZHANG P Y,et al.Preparation,characterization and properties of nano Au-TiO2composite thin films by sol-gel process[J].Chemical journal of Chinese universities,2002,23(8):1574-1578.
[28]张丽仙,赵铱民,邵龙泉,等.牙用镍铬合金表面不同涂层电化学腐蚀研究[J].实用口腔医学杂志,2009,25(4):471-474.ZHANG L X,ZHAO Y M,SHAO L Q,et al.A research on the corrosion resistance of Ni-Cr alloy with different coatings[J].Journal of practical stomatology,2009,25(4):471-474.
[29]刘维民,薛群基,周静芳,等.纳米颗粒的抗磨作用及作为磨损修复添加剂的应用研究[J].中国表面工程,2001,14(3):21-23.LIU W M,XUE Q J,ZHOU J F,et al.The anti wear function of nanoparticles and their application in abrasion repairing additive[J].China surface engineering,2001,14(3):21-23.
[30]张蕊,王鲁宁,赵飞,等.贵金属在船用钛及钛合金表面改性中的应用[J].贵金属,2017,38(4):74-80.ZHANG R,WANG L N,ZHAO F,et al.Application and development trend of precious metals in the surface modification of marine titanium and titanium alloys[J].Precious metals,2017,38(4):74-80.
[31]BAHADUR S,SUNKARA C.Effect of transfer film structure,composition and bonding on the tribological behavior of polyphenylene sulfide filled with nano particles of TiO2,ZnO,CuO and SiC[J].Wear,2005,258(9):1411-1421.
[32]OKINAKA Y.Significance of inclusions in electroplated gold films for electronics applications[J].Gold bulletin,2000,33(4):117-127.
[33]杨长江,陈国需,赵立涛,等.纳米软金属作为自修复润滑添加剂的研究进展[J].润滑与密封,2009,34(5):115-117.YANG C J,CHEN G X,ZHAO L T,et al.Research progress of soft metal nanoparticles as self-repairing lubricant additive[J].Lubrication and sealing,2009,34(5):115-117.
[34]方芬,颜红侠,张军平.纳米粒子在润滑材料中的应用进展[J].材料保护,2006,39(12):32-36.FANG F,YAN H X,ZHANG J P.Application progress of nanoparticles in lubricating materials[J].Material protection,2006,39(12):32-36.
[35]于立岩,郝春成,隋丽娜,等.纳米粒子改善润滑油摩擦磨损性能的研究[J].材料科学与工程学报,2004,22(6):901-905.YU L Y,HAO C C,SUI L N,et al.Study on the improving friction and wear properties of lubricating oil with nanoparticles[J].Journal of materials science and engineering,2004,22(6):901-905.
[36]于德洋,翁立军,欧阳锦林.空间机械润滑研究的发展现状[J].摩擦学学报,1996,16(1):89-96.YU D Y,WENG L J,OUYANG J L.Current development situation of space mechanical lubrication[J].Journal of tribology,1996,16(1):89-96.
[37]ROBERTS E W,WILLIAMS B J,OGILVY J A.The effect of substrate surface roughness on the friction and wear of sputtered MoS2 films[J].Journal of physics DApplied physics,1992,25(1A):A65.
[38]KONG L,ZHU S,QIAO Z,et al.Effect of Mo and Ag on the friction and wear behavior of ZrO2,(Y2O3)-AgCaF2-Mo composites from 20°C to 1000°C[J].Tribology international,2014,78(78):7-13.
[39]STOYANOV P,GUPTA S,CHROMIK R R,et al.Microtribological performance of Au-MoS2 nanocomposite and Au/MoS2 bilayer coatings[J].Tribology international,2012,52(3):144-152.
[40]DAI L Y,MENG R G,CHEN J F,et al.Research progress on nanoparticles for metal wear self-repairing[J].China ship repair,2012,25(04):33-36.
[41]郑林庆.摩擦学原理[M].北京:高等教育出版社,1994.ZHENG L Q.Principles of tribology[M].Beijing:Higher Education Press,1994.
[42]王新平,肖金坤,张雷,等.载荷对AuNi9/金镀层摩擦副摩擦磨损性能的影响[J].中国有色金属学报,2012,22(12):3427-3431.WANG X P,XIAO J K,ZHANG L,et al.Effect of load on friction and wear behavior of AuNi9/Au coating tribocouple[J].The Chinese journal of nonferrous metals,2012,22(12):3427-3431.
[43]STOYANOV P,CHROMIK R R,GOLDBAUM D,et al.Microtribological performance of Au-MoS2,and Ti-MoS2,coatings with varying contact pressure[J].Tribology letters,2010,40(1):199-211.
[44]LI J,ZHANG H,FAN A,et al.Tribological properties characterization of Ti/Cu/N thin films prepared by DCmagnetron sputtering on titanium alloy[J].Surface and coatings technology,2016,294:30-35.
[45]ANTLER M,DROZDOWICZ M H.Fretting corrosion of gold-plated connector contacts[J].Wear,1981,74(1):27-50.
[46]WANG Y,YING J,WEI S,et al.Au-Ni-TiO2 nanocomposite coatings prepared by sol-enhanced method[J].Journal of the electrochemical society,2014,161(14):775-781.
[47]王其明,徐锦芬,党鸿辛.MoS2-Au共溅膜的结构与性能之研究[J].摩擦学学报,1990,10(2):84-95.WANG Q M,XU J F,DANG X H.A study on the structures and performances of MoS2-Au co-sputtered films[J].Tribology,1990,10(2):84-95
[48]LIN S S,HUANG J L,?AJGALIK P.The properties of heavily Al-doped ZnO films before and after annealing in the different atmosphere[J].Thin solid films,2004,185(2/3):254-263.
[49]TORRELL M,CUNHA L,CAVALEIRO A,et al.Functional and optical properties of Au:TiO2,nanocomposite films:The influence of thermal annealing[J].Applied surface science,2010,256(22):6536-6542.
[50]HVOLB?K B,JANSSENS T V W,CLAUSEN B S,et al.Catalytic activity of Au nanoparticles[J].Nano today,2007,2(4):14-18.
[51]LI G,WANG Y,CAO Z.Effect of refined grain size on corrosion behavior of metal Cr in media containing chloride ions[J].Ciesc journal,2012,63(2):560-566.
[52]SHORES D A.Corrosion and metal release rates of Ni substrates under a porous gold coating[J].Corrosion science,2008,50(2):372-383.
[53]BUELENS C,CELIS J P,ROOS J R.Electrochemical aspects of the plating of gold and composite gold-alumina[J].Transactions of the IMF,1985,63(1):6-10.
[54]GUZMáN P,APERADOR W,YATE L.Enhancement of the pitting corrosion resistance of AISI 316LVM steel with Ta-Hf-C/Au bilayers for biomedical applications[J].Journal of nanomaterials,2017(1):1-10.
© 2004-2018 中国地质图书馆版权所有 京ICP备05064691号 京公网安备11010802017129号 地址：北京市海淀区学院路29号 邮编：100083 电话：办公室：(+86 10)66554848；文献借阅、咨询服务、科技查新：66554700 |