摘要
在UHPC材料中,通过在粉煤灰0%、20%、30%、40%的掺量下掺入不同碱激发剂(氢氧化钙、氢氧化钠、硫酸钠、硫酸钙、碳酸钠、水玻璃)测试砂浆浆体流动性、经时损失和胶砂试件抗压强度、抗折强度。结果表明:在UHPC材料中,随着粉煤灰掺量的增加,流动性改善明显,对抗压抗折强度影响较大;在粉煤灰掺量较小时,碱激发剂效果不明显,随着粉煤灰掺量的增加,碱激发剂的效果逐渐凸显出来;在粉煤灰掺量为30%、40%时,硫酸钙为最为突出的碱激发剂。
In UHPC materials,the fluidity,time-consuming loss,compressive strength and flexural strength of mortar specimens were tested by adding different alkali activators(calcium hydroxide,sodium hydroxide,sodium sulfate,calcium sulfate,sodium carbonate,sodium silicate) at the content of 0%,20%,30% and 40% fly ash.The results show that in UHPC materials,with the increase of fly ash content,the fluidity improves obviously,which has a great influence on the compressive and flexural strength; when the fly ash content is small,the effect of alkali activator is not obvious;with the increase of fly ash content,the effect of alkali activator is gradually prominent; when the fly ash content is 30%or 40%,calcium sulfate is the most prominent alkali activator.
引文
[1]PALOMO A,FERNANDEZ-JIMENEZ A.Opcfly ash cementitious systems:study of gel binders produced during alkaline hydration[J].Journal of materials science,2007,42(9):2958-2966.
[2]史才军,何富强.碱激发水泥的类型与特点[J].硅酸盐学报,2012(01):69-75.