以纤维素、淀粉为还原剂,在特制高压反应釜内反应4h,探讨原料配比、还原温度及固液比对还原Fe_2O_3的影响,并借助XRD及SEM等分析了不同还原条件下还原产物的微观形貌及物相组成。结果表明,在Fe_2O_3粉末、氢氧化钠、淀粉用量分别为50%、25%、25%,温度310℃、固液比3∶20、搅拌速度420r/min的条件下,最高还原率为97%。
Effects of raw materials ratio,reduction temperature and ratio of solid to liquid on reduction of Fe_2O_3 were investigated in special high-pressure reactor for 4 happlying cellulose and starch as reductant respectively.Microstructure and phase composition of the reduction products under different reduction conditions were analyzed by XRD and SEM.The results show that the highest reduction rate is 97%under the conditions including mass ratio of Fe_2O_3 powder,sodium hydroxide,and starch dosage of 50%,25%,and 25%,temperature of 310℃,ratio of solid to liquid of 3∶20,and stirring speed of 420 r/min.
引文
[1]徐匡迪.低碳经济与钢铁工业[J].钢铁,2010,45(3):1-12.
[2]张利民,李静,孟彬,等.绿色钢铁工业发展对策研究[J].科技视界,2015(2):15-18.
[3]殷瑞钰,张春霞.钢铁企业功能拓展是实现循环经济的有效途径[J].钢铁,2005,40(7):1-9.
[4]范晓慧,袁晓丽,姜涛,等.铁精矿粒度对球团强度的影响[J].中国有色金属学报,2006,16(11):1965-1968.
[5]王昌安,罗廉明.铁精矿粒度组成对球团质量的影响[J].武汉化工学院学报,2005,27(2):38-42.
[6]傅菊英,李云涛,姜昌伟,等.磁铁精矿球团氧化动力学[J].中南工业大学学报,2004,35(6):950-955.
[7]姜昌伟,傅菊英,李思导.凹山磁铁精矿球团焙烧特性研究[J].中南工业大学学报,2004,35(6):435-439.
[8]牛宏坤,王一雍,宁哲,等.高压水热还原法利用生物质分离黄钾铁矾渣中铁的研究[J].有色金属(冶炼部分),2017(7):1-3.