采用理论分析,探讨了涂层粒子厚度与粒子大小对防刺性的影响。同时,通过实验制备了硬质粒子与聚丙烯酸酯涂层织物,讨论了不同加工工艺对防刺性能的影响。通过分析发现,涂层厚度h与粒子半径r的比值越大,织物的防刺性越好。实验结果表明,粒子粒径为5μm,涂层厚度为100μm,涂层温度为64℃,颗粒与粘结剂比为2:3时,织物的防刺性能最好。
Based on theoretical analysis, the effects of coating particle thickness and particle size on the stab resistance were discussed. Hard particle and polyacrylate coated fabric was prepared to discuss the effects of different processing techniques on the stab resistance. It was found that the stab resistance of the fabric was better when the ratio of coating thickness h to particle radius r was larger. And when particle size was 5 micron, coating thickness was 100 micron, coating temperature was 64 ℃ and particle and binder ratio reached 2:3, the stab resistance of the fabric was best.
引文
[1] 戴瑞玉,蒋玲玲,张莉,等.高危从业人员防刺服探讨概论[J].中国纤检,2012(2):86-87.
[2] 余科.防刺服用材料浅析[J].现代丝绸科学与技术,2008,23(6):35-37.
[3] 袁梦琦,钱新明,蒋锦辉,等.鳞甲式防刺芯片及用其制成的防刺装备:中国,105403106A[P].2016.
[4] 黎国标,黎国光,兰宦国.一种非金属防刺材料的制备方法:中国,105316951 A[P].2016.
[5] 钟智丽,薛兆磊,孙涵,等.三维机织物防刺性能研究[J].纺织科学与工程学报,2018,35(4):19-23.
[6] 张为成.一种新型工程材料—立方氮化硼[J].机械工程师,1980(2):40-41.
[7] 邱冠雄,姜亚明.人体装甲与高性能纤维[J].针织工业,2003(2):62-65.
[8] 王越.一种防刺服:中国,2092736[P].1992.
[9] GB/T230.1-2009.金属材料洛氏硬度实验标准[S].中国质检总局.2009.