文摘
Diketopyrrolopyrrole (DPP)-based conjugated polymer PDTDPPQT was synthesized and was used to perform epitaxial polymer crystal growth on removable 1,3,5-trichlorobenzene crystallite templates. A thin-film transistor (TFT) was successfully fabricated in well-grown large spherulites of PDTDPPQT. The charge carrier mobility along the radial direction of the spherulites was measured to be 5.46鈥?2.04 cm2 V鈥? s鈥?, which is significantly higher than that in the direction perpendicular to the radial direction. The dynamic response of charge transport was also investigated by applying a pulsed bias to TFTs loaded with a resistor (鈭?0 M惟). The charge-transport behaviors along the radial direction and perpendicular to the radial direction were investigated by static and dynamic experiments through a resistor-loaded (RL) inverter. The RL inverter made of PDTDPPQT-based TFT operates well, maintaining a fairly high switching voltage ratio (VoutON/VoutOFF) at a relatively high frequency when the source-drain electrodes are aligned parallel to the radial direction.