摘要
Shell-core Fe-Sr0.8La0.2Fe11.8Co0.2O19 composites are prepared by chemical vapor deposition (CVD) for use as microwave absorbing materials. Scanning electron microscopy and X-ray diffraction analyses show that the CVD method yields Sr0.8La0.2Fe11.8Co0.2O19 powders with a uniform coating of Fe. Compared with Sr0.8La0.2Fe11.8Co0.2O19, Fe-Sr0.8La0.2Fe11.8Co0.2O19 composites have higher electrical conductivity, permittivity, and dielectric loss, which gradually increase with increasing Fe content. When Sr0.8La0.2Fe11.8Co0.2O19/Fe=7:3, a reflection loss (RL) exceeding 鈭?0 dB is obtained in the frequency range of 10-14 GHz at a coating thickness of 2.0 mm. A minimum RL of 鈭?0 dB was found at 8.0 GHz, corresponding to a matching thickness of 2.8 mm.