Nanocrystaline solid solution CeO₂-Bi₂O₃

详细信息	查看全文 | 推荐本文 |

• 作者：M. Prekajski^a ; ^{prekajski@vinca.rs} ; Z. Doh&#269 ; evi&#263 ; -Mitrovi&#263 ; ^b ; M. Radovi&#263 ; ^b ; B. Babi&#263 ; ^a ; J. Panti&#263 ; ^a ; A. Kremenovi&#263 ; ^c ; B. Matovi&#263 ; ^a
• 关键词：Self-propagating reaction ; CeO2 ; Bi2O3 ; X-ray methods ; Spectroscopy
• 刊名：Journal of the European Ceramic Society
• 出版年：2012
• 期刊代码：53_09552219
• 类别：ms
• 出版时间：July, 2012
• 卷：32
• 期：9
• 页码：1983-1987
• 文件大小：452 K

摘要

Nanocrystalline powders of solid solution CeO₂-Bi₂O₃ were synthesized by self-propagating room temperature reaction (SPRT) procedure with composition (Ce_1鈭?em>xBi_xO_2鈭?em>未 where the x = 0.1-0.5). X-ray diffraction analyses show that for x < 0.50 a solid solution with fluorite structure is formed. Rietveld's structure refinement method was applied to characterize prepared powders and its microstructure (size-strain). The lattice parameters increase according to Vegard's rule with increasing of Bi concentration. The average crystallite size is about 2-3 nm. Spectroscopic ellipsometry and Raman scattering measurements were used to characterize the samples at room temperature. The Raman measurements demonstrated electron molecular vibrational coupling and increase of oxygen vacancy concentration whereas increase of Bi content provokes a small decrease of optical absorption edge in comparison with pure ceria. Specific surface area of obtained powders was measured by Brunauer-Emmet-Teller (BET) method.