对低滚动阻力轿车轮胎胎面胶配方进行优化。结果表明,通过调整生胶体系(采用天然橡胶/顺丁橡胶/溶聚丁苯橡胶并用胶),减小环保芳烃油RAE用量,胶料的门尼粘度减小,门尼焦烧时间延长,硫化速度加快,硫化胶的物理性能和耐老化性能提高,工艺性能良好,成品轮胎的耐久性能和高速性能达到国家标准要求,滚动阻力降低。
The formulation of tread compound for low rolling resistance passenger car tire was optimized. The results showed that,by adjusting the raw rubber system(blend of natural rubber/cis-butadiene rubber/solution polymerized styrene-butadiene rubber)and decreasing the addition level of environmental friendly aromatic oil RAE,the Mooney viscosity of the compound decreased,the Mooney scorching time was extended and the curing rate increased. The physical properties and aging resistance of the vulcanizate were improved,and the processability was good. The endurance and high speed performance of the finished tire met the requirements of the national standard and the rolling resistance decreased.
引文
[1]王梦蛟.绿色轮胎的发展及其推广应用[J].橡胶工业,2018,65(1):105-112.
[2]顾培霜,郑昆,陈松.低滚动阻力抗湿滑轿车胎的开发[J].世界橡胶工业,2014,41(12):1-3.
[3]刘琦,孙学红,李文东,等.低滚动阻力胎面胶配方优化设计[J].轮胎工业,2017,37(8):471-474.
[4]周宏斌,王宝全,张元洪,等.低滚动阻力载重子午线轮胎配方开发[J].橡胶工业,2017,64(2):99-103.