作者关键词:Al alloy;texture;deformation;recrystallization;precipitation state
起始页:292
总页数:4
刊名:材料与冶金学报
是否内版:否
刊频:季刊
创刊时间:2002
主办单位:东北大学
主编:左良
地址:沈阳市文化路3号巷11号东北大学114信箱
邮编:110004
电子信箱:huji@chinajournal.net.cn
卷:5
期:4
期刊索取号:P750.6 334
摘要
The deformation and recrystallization textures of 6111 Al alloy with various precipitation stateshave been investigated by means of the orientation distribution functions(O DFs). I t was found that the precipitationstate had significant efects on both rolling and recrystallization textures of Al alloy. For the alloywith no or little precipitate, the orientation intensities were distributed more homogeneously along the p-fiber.With increasing aging temperature, the orientation intensities along the ,B-fiber increased firstly and decreasedthen. Simultaneity, the orientation intensities along the f3-fiber were distributed more and more inhomogeneously.On the other hand, with the precipitates increasing the recrystallization textures changed graduallyfrom( 001 ) < UVW> and very weak l 0111 < 111> orientation to the strong(001)<311>and(011)<11>orientation.