- 中文主题词：锰 ; 含量测定 ; 原子发射光谱法 ; 光谱化学分析 ; 试验方法 ; 钢
- 标准号：ASTM E2209-2002(2006)e1
- 发布日期：2002
- 英文题名：Standard Test Method for Analysis of High Manganese Steel Using Atomic Emission Spectrometry
- 英文主题词：high manganese steel ; atomic emission ; point-to-plane technique ; spectrometric analysis
- 标准状态：现行
- 发布单位：US-ASTM
- 国际标准分类号：77.040.30 (Chemical analysis of metals)
- 载体形态：6P.;A4
- 中国标准分类号：H11
- 国别：美国材料与试验协会
The chemical composition of high manganese steel alloys must be determined accurately to ensure the desired metallurgical properties. This procedure is suitable for manufacturing control and inspection testing.
1.1 This method provides for the analysis of high manganese steel by atomic emission spectrometry using the point-to-plane technique for the following elements in the concentration ranges shown:
| Elements | Concentration Range, % |
| Aluminum (Al) | 0.02 to 0.15 |
| Carbon (C) | 0.3 to 1.4 |
| Chromium (Cr) | 0.25 to 2.00 |
| Manganese (Mn) | 8.0 to 16.2 |
| Molybdenum (Mo) | 0.03 to 2.0 |
| Nickel (Ni) | 0.05 to 4.0 |
| Phosphorus (P) | 0.025 to 0.06 |
| Silicon (Si) | 0.25 to 1.5 |
Note 18212;The ranges represent the actual levels at which this method was tested. These concentration ranges can be extended to higher concentrations by the use of suitable reference materials. Sulfur is not included because differences in results between laboratories exceeded acceptable limits at all analyte levels.
1.2 This test method may involve hazardous materials, operations, and equipment. This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.