Preparation, characterization and properties of fiber reinforced composites using silicon-containing hybrid polymers

详细信息    查看全文

• 作者：Mingfeng Chen and Canpei Liu
• 刊名：Polymers for Advanced Technologies
• 出版年：2017
• 出版时间：February 2017
• 年：2017
• 卷：28
• 期：2
• 页码：145-151
• 全文大小：401K
• ISSN：1099-1581

文摘

A novel glass fiber reinforced composite was prepared by using silicon-containing hybrid polymers, poly(methylhydrogen-diethynylsilyene) (PMES) and poly(phenylethynyl-silyloxide-phenylborane) (APABS), as matrix resins. The curing behavior and rheological properties of the matrix resins were investigated by differential scanning calorimetry (DSC) and rotational rheometer. The dynamic viscoelastic properties, mechanical properties, and microstructures of the composites were studied by dynamic mechanical analysis (DMA), universal testing machine (UTM), and scanning electron microscopy (SEM), respectively. The results show that the composite can be well cured between 200 and 300 °C through reactive groups like Si-H, N-H, and C≡C units, the possible thermosetting mechanism is also proposed. The composites exhibit excellent mechanical properties with bending strength reach up to 261 and 178 MPa before and after heat-treating, respectively. SEM analysis clearly indicates that crack in the matrix, matrix/fiber interface debonding, and fiber pull out are predominate failure mechanism for the composites which are heat-treated in different temperatures. All these obtained results can give theoretical guiding reference for their further applications. Copyright