Mesoporous γ-Iron Oxide Nanoparticles for Magnetically Triggered Release of Doxorubicin and Hyperthermia Treatment
详细信息    查看全文
文摘
Mesoporous iron-oxide nanoparticles (mNPs) were prepared by using a modified nanocasting approach with mesoporous carbon as a hard template. mNPs were first loaded with doxorubicin (Dox), an anticancer drug, and then coated with the thermosensitive polymer Pluronic F108 to prevent the leakage of Dox molecules from the pores that would otherwise occur under physiological conditions. The Dox-loaded, Pluronic F108-coated system (Dox@F108-mNPs) was stable at room temperature and physiological pH and released its Dox cargo slowly under acidic conditions or in a sudden burst with magnetic heating. No significant toxicity was observed in vitro when Dox@F108-mNPs were incubated with noncancerous cells, a result consistent with the minimal internalization of the particles that occurs with normal cells. On the other hand, the drug-loaded particles significantly reduced the viability of cervical cancer cells (HeLa, IC50=0.70 μm), wild-type ovarian cancer cells (A2780, IC50=0.50 μm) and Dox-resistant ovarian cancer cells (A2780/AD, IC50=0.53 μm). In addition, the treatment of HeLa cells with both Dox@F108-mNPs and subsequent alternating magnetic-field-induced hyperthermia was significantly more effective at reducing cell viability than either Dox or Dox@F108-mNP treatment alone. Thus, Dox@F108-mNPs constitute a novel soft/hard hybrid nanocarrier system that is highly stable under physiological conditions, temperature-responsive, and has chemo- and thermotherapeutic modes of action.

© 2004-2018 中国地质图书馆版权所有 京ICP备05064691号 京公网安备11010802017129号

地址:北京市海淀区学院路29号 邮编:100083

电话:办公室:(+86 10)66554848;文献借阅、咨询服务、科技查新:66554700