Influence of hydrogen on defect generation during shock-loading of Pd was examined.
Shock-loading introduced dislocations and vacancies.
Deformation-induced vacancies agglomerated into clusters consisting of 2–3 vacancies.
Absorbed hydrogen facilitates generation of both dislocations and vacancies.