Further straining through cold-rolling was imposed to two-pass CGPed sheets.
Post-annealing effect at 150, 250 and 350 °C was studied for Al-Mn-Si specimens.
Evolutions of microstructure and intermetallic particles were characterized.
Mechanical properties of different rolled CGPed samples were examined.