In this work, 伪-Al2O3 (1-40 vol%) particles (350 nm) were added to a 19.58Li2O路11.10ZrO2路69.32SiO2 (5 碌m) glass-ceramic matrix to prepare composites with the purpose of studying the influence of 伪-Al2O3 on their mechanical, thermal and electrical properties in order to obtain materials for LTCCs applications. The composites, sintered between 800 and 950 掳C for 30 min, with relative densities between 85% and 93%, showed zircon and 尾-spodumene as main crystalline phases. The maximum bending strength (290 MPa) was achieved for composites with 1% 伪-Al2O3. For composites containing between 1% and 10% 伪-Al2O3, sintered at 900 掳C/30 min, the electrical and thermal conductivities and CTE varied between 3.35 and 1.21脳10鈭?0 S/cm, 4.65 and 2.98 W/m K, 9.54 and 3.36脳10鈭? 掳C鈭?, respectively.